Nickel Beryllium 360 vs. SAE-AISI 9310 Steel

Nickel beryllium 360 belongs to the nickel alloys classification, while SAE-AISI 9310 steel belongs to the iron alloys. There are 24 material properties with values for both materials. Properties with values for just one material (8, in this case) are not shown.

For each property being compared, the top bar is nickel beryllium 360 and the bottom bar is SAE-AISI 9310 steel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 200
190
Elongation at Break, % 1.0 to 30
17 to 19
Fatigue Strength, MPa 260 to 710
300 to 390
Poisson's Ratio 0.3
0.29
Shear Modulus, GPa 77
73
Shear Strength, MPa 510 to 1100
510 to 570
Tensile Strength: Ultimate (UTS), MPa 780 to 1860
820 to 910
Tensile Strength: Yield (Proof), MPa 380 to 1590
450 to 570

Thermal Properties

Melting Completion (Liquidus), °C 1330
1460
Melting Onset (Solidus), °C 1200
1420
Specific Heat Capacity, J/kg-K 460
470
Thermal Conductivity, W/m-K 48
48
Thermal Expansion, µm/m-K 14
13

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 5.0
7.7
Electrical Conductivity: Equal Weight (Specific), % IACS 5.4
8.9

Otherwise Unclassified Properties

Density, g/cm3 8.3
7.9

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 12 to 190
120 to 150
Resilience: Unit (Modulus of Resilience), kJ/m3 360 to 3440
540 to 860
Stiffness to Weight: Axial, points 13
13
Stiffness to Weight: Bending, points 24
24
Strength to Weight: Axial, points 26 to 62
29 to 32
Strength to Weight: Bending, points 23 to 41
25 to 27
Thermal Diffusivity, mm2/s 13
13
Thermal Shock Resistance, points 19 to 46
24 to 27

Comparable Variants