PA 6/12 vs. PGA
Both PA 6/12 and PGA are thermoplastics. There are 10 material properties with values for both materials. Properties with values for just one material (9, in this case) are not shown.
For each property being compared, the top bar is PA 6/12 and the bottom bar is PGA.
Metric UnitsUS Customary Units
Material Properties
| Density, g/cm3 | 1.1 | |
| 1.5 |
| Elastic (Young's, Tensile) Modulus, GPa | 1.7 to 2.2 | |
| 6.5 |
| Elongation at Break, % | 30 to 120 | |
| 1.0 |
| Maximum Temperature: Decomposition, °C | 450 | |
| 260 |
| Melting Onset (Solidus), °C | 210 | |
| 230 |
| Stiffness to Weight: Axial, points | 0.89 to 1.2 | |
| 2.4 |
| Stiffness to Weight: Bending, points | 38 to 41 | |
| 41 |
| Strength to Weight: Axial, points | 10 to 15 | |
| 10 |
| Strength to Weight: Bending, points | 25 to 31 | |
| 21 |
| Tensile Strength: Ultimate (UTS), MPa | 40 to 58 | |
| 55 |