PGA vs. PA 6/10

Both PGA and PA 6/10 are thermoplastics. There are 10 material properties with values for both materials. Properties with values for just one material (11, in this case) are not shown.

For each property being compared, the top bar is PGA and the bottom bar is PA 6/10.

Metric UnitsUS Customary Units

Material Properties

Density, g/cm3 1.5
1.1
Elastic (Young's, Tensile) Modulus, GPa 6.5
1.6 to 2.3
Elongation at Break, % 1.0
110 to 120
Maximum Temperature: Decomposition, °C 260
440
Melting Onset (Solidus), °C 230
220
Stiffness to Weight: Axial, points 2.4
0.78 to 1.1
Stiffness to Weight: Bending, points 41
34 to 39
Strength to Weight: Axial, points 10
11 to 15
Strength to Weight: Bending, points 21
25 to 30
Tensile Strength: Ultimate (UTS), MPa 55
45 to 60