PGA vs. PBI
PGA belongs to the thermoplastics classification, while PBI belongs to the thermoset plastics. There are 9 material properties with values for both materials. Properties with values for just one material (20, in this case) are not shown.
For each property being compared, the top bar is PGA and the bottom bar is PBI.
Metric UnitsUS Customary Units
Material Properties
| Density, g/cm3 | 1.5 | |
| 1.3 |
| Elastic (Young's, Tensile) Modulus, GPa | 6.5 | |
| 5.9 |
| Elongation at Break, % | 1.0 | |
| 3.0 |
| Maximum Temperature: Decomposition, °C | 260 | |
| 590 |
| Stiffness to Weight: Axial, points | 2.4 | |
| 2.5 |
| Stiffness to Weight: Bending, points | 41 | |
| 46 |
| Strength to Weight: Axial, points | 10 | |
| 34 |
| Strength to Weight: Bending, points | 21 | |
| 50 |
| Tensile Strength: Ultimate (UTS), MPa | 55 | |
| 160 |