PGA vs. UHMW-PE
Both PGA and UHMW-PE are thermoplastics. There are 9 material properties with values for both materials. Properties with values for just one material (10, in this case) are not shown.
For each property being compared, the top bar is PGA and the bottom bar is UHMW-PE.
Metric UnitsUS Customary Units
Material Properties
| Density, g/cm3 | 1.5 | |
| 0.94 |
| Elastic (Young's, Tensile) Modulus, GPa | 6.5 | |
| 0.8 |
| Elongation at Break, % | 1.0 | |
| 400 |
| Melting Onset (Solidus), °C | 230 | |
| 130 |
| Stiffness to Weight: Axial, points | 2.4 | |
| 0.47 |
| Stiffness to Weight: Bending, points | 41 | |
| 33 |
| Strength to Weight: Axial, points | 10 | |
| 14 |
| Strength to Weight: Bending, points | 21 | |
| 32 |
| Tensile Strength: Ultimate (UTS), MPa | 55 | |
| 49 |