PPO vs. LCP
Both PPO and LCP are thermoplastics. There are 10 material properties with values for both materials. Properties with values for just one material (13, in this case) are not shown.
For each property being compared, the top bar is PPO and the bottom bar is LCP.
Metric UnitsUS Customary Units
Material Properties
| Density, g/cm3 | 1.1 to 1.4 | |
| 1.4 to 1.6 |
| Elongation at Break, % | 3.5 to 28 | |
| 1.0 to 3.0 |
| Flexural Modulus, GPa | 2.5 to 8.6 | |
| 9.0 to 23 |
| Flexural Strength, MPa | 92 to 140 | |
| 160 to 320 |
| Heat Deflection Temperature At 1.82 MPa (264 psi), °C | 120 to 140 | |
| 240 to 270 |
| Limiting Oxygen Index (LOI), % | 32 | |
| 35 |
| Specific Heat Capacity, J/kg-K | 1020 to 1250 | |
| 1020 to 1200 |
| Strength to Weight: Axial, points | 16 to 27 | |
| 33 to 43 |
| Strength to Weight: Bending, points | 33 to 42 | |
| 45 to 56 |
| Tensile Strength: Ultimate (UTS), MPa | 63 to 140 | |
| 180 to 230 |