SAE-AISI 1016 Steel vs. Solder Alloy 301
SAE-AISI 1016 steel belongs to the iron alloys classification, while solder alloy 301 belongs to the otherwise unclassified metals. There are 26 material properties with values for both materials. Properties with values for just one material (6, in this case) are not shown.
For each property being compared, the top bar is SAE-AISI 1016 steel and the bottom bar is solder alloy 301.
Metric UnitsUS Customary Units
Mechanical Properties
| Brinell Hardness | 120 to 140 | |
| 23 |
| Elastic (Young's, Tensile) Modulus, GPa | 190 | |
| 40 |
| Elongation at Break, % | 21 to 28 | |
| 51 |
| Poisson's Ratio | 0.29 | |
| 0.34 |
| Shear Modulus, GPa | 73 | |
| 15 |
| Tensile Strength: Ultimate (UTS), MPa | 430 to 480 | |
| 55 |
| Tensile Strength: Yield (Proof), MPa | 240 to 390 | |
| 49 |
Thermal Properties
| Latent Heat of Fusion, J/g | 250 | |
| 55 |
| Melting Completion (Liquidus), °C | 1460 | |
| 140 |
| Melting Onset (Solidus), °C | 1420 | |
| 140 |
| Specific Heat Capacity, J/kg-K | 470 | |
| 160 |
| Thermal Conductivity, W/m-K | 52 | |
| 19 |
| Thermal Expansion, µm/m-K | 12 | |
| 14 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 7.0 | |
| 4.7 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 8.0 | |
| 4.9 |
Otherwise Unclassified Properties
| Density, g/cm3 | 7.9 | |
| 8.7 |
| Embodied Carbon, kg CO2/kg material | 1.4 | |
| 13 |
| Embodied Energy, MJ/kg | 18 | |
| 210 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 92 to 100 | |
| 27 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 150 to 410 | |
| 30 |
| Stiffness to Weight: Axial, points | 13 | |
| 2.5 |
| Stiffness to Weight: Bending, points | 24 | |
| 13 |
| Strength to Weight: Axial, points | 15 to 17 | |
| 1.8 |
| Strength to Weight: Bending, points | 16 to 17 | |
| 3.7 |
| Thermal Diffusivity, mm2/s | 14 | |
| 13 |
| Thermal Shock Resistance, points | 13 to 15 | |
| 7.2 |
Alloy Composition
| Aluminum (Al), % | 0 | |
| 0 to 0.0010 |
| Antimony (Sb), % | 0 | |
| 0 to 0.1 |
| Arsenic (As), % | 0 | |
| 0 to 0.030 |
| Bismuth (Bi), % | 0 | |
| 56.5 to 59 |
| Cadmium (Cd), % | 0 | |
| 0 to 0.0020 |
| Carbon (C), % | 0.13 to 0.18 | |
| 0 |
| Copper (Cu), % | 0 | |
| 0 to 0.050 |
| Gold (Au), % | 0 | |
| 0 to 0.050 |
| Indium (In), % | 0 | |
| 0 to 0.1 |
| Iron (Fe), % | 98.8 to 99.27 | |
| 0 to 0.020 |
| Lead (Pb), % | 0 | |
| 0 to 0.070 |
| Manganese (Mn), % | 0.6 to 0.9 | |
| 0 |
| Nickel (Ni), % | 0 | |
| 0 to 0.010 |
| Phosphorus (P), % | 0 to 0.040 | |
| 0 |
| Silver (Ag), % | 0 | |
| 0 to 0.1 |
| Sulfur (S), % | 0 to 0.050 | |
| 0 |
| Tin (Sn), % | 0 | |
| 41 to 43 |
| Zinc (Zn), % | 0 | |
| 0 to 0.0010 |