SAE-AISI 1044 Steel vs. EN 1.4317 Stainless Steel

Both SAE-AISI 1044 steel and EN 1.4317 stainless steel are iron alloys. They have 82% of their average alloy composition in common. There are 29 material properties with values for both materials. Properties with values for just one material (6, in this case) are not shown.

For each property being compared, the top bar is SAE-AISI 1044 steel and the bottom bar is EN 1.4317 stainless steel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 190
190
Elongation at Break, % 18
17
Fatigue Strength, MPa 230
380
Poisson's Ratio 0.29
0.28
Shear Modulus, GPa 72
76
Tensile Strength: Ultimate (UTS), MPa 620
860
Tensile Strength: Yield (Proof), MPa 340
630

Thermal Properties

Latent Heat of Fusion, J/g 250
280
Maximum Temperature: Mechanical, °C 400
770
Melting Completion (Liquidus), °C 1460
1440
Melting Onset (Solidus), °C 1420
1400
Specific Heat Capacity, J/kg-K 470
480
Thermal Conductivity, W/m-K 51
26
Thermal Expansion, µm/m-K 12
11

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 7.0
2.7
Electrical Conductivity: Equal Weight (Specific), % IACS 8.0
3.2

Otherwise Unclassified Properties

Base Metal Price, % relative 1.8
10
Density, g/cm3 7.8
7.8
Embodied Carbon, kg CO2/kg material 1.4
2.4
Embodied Energy, MJ/kg 18
33
Embodied Water, L/kg 45
110

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 94
130
Resilience: Unit (Modulus of Resilience), kJ/m3 320
1010
Stiffness to Weight: Axial, points 13
14
Stiffness to Weight: Bending, points 24
25
Strength to Weight: Axial, points 22
31
Strength to Weight: Bending, points 21
26
Thermal Diffusivity, mm2/s 14
7.0
Thermal Shock Resistance, points 20
30

Alloy Composition

Carbon (C), % 0.43 to 0.5
0 to 0.060
Chromium (Cr), % 0
12 to 13.5
Iron (Fe), % 98.8 to 99.27
78.7 to 84.5
Manganese (Mn), % 0.3 to 0.6
0 to 1.0
Molybdenum (Mo), % 0
0 to 0.7
Nickel (Ni), % 0
3.5 to 5.0
Phosphorus (P), % 0 to 0.040
0 to 0.035
Silicon (Si), % 0
0 to 1.0
Sulfur (S), % 0 to 0.050
0 to 0.025