SAE-AISI 1049 Steel vs. AWS E80C-B3L
Both SAE-AISI 1049 steel and AWS E80C-B3L are iron alloys. They have a very high 96% of their average alloy composition in common. There are 27 material properties with values for both materials. Properties with values for just one material (6, in this case) are not shown.
For each property being compared, the top bar is SAE-AISI 1049 steel and the bottom bar is AWS E80C-B3L.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 190 | |
| 190 |
| Elongation at Break, % | 11 to 17 | |
| 19 |
| Poisson's Ratio | 0.29 | |
| 0.29 |
| Shear Modulus, GPa | 72 | |
| 73 |
| Tensile Strength: Ultimate (UTS), MPa | 680 to 750 | |
| 620 |
| Tensile Strength: Yield (Proof), MPa | 370 to 640 | |
| 540 |
Thermal Properties
| Latent Heat of Fusion, J/g | 250 | |
| 260 |
| Melting Completion (Liquidus), °C | 1460 | |
| 1460 |
| Melting Onset (Solidus), °C | 1420 | |
| 1420 |
| Specific Heat Capacity, J/kg-K | 470 | |
| 470 |
| Thermal Conductivity, W/m-K | 51 | |
| 41 |
| Thermal Expansion, µm/m-K | 12 | |
| 13 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 7.0 | |
| 7.7 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 8.1 | |
| 8.8 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 1.8 | |
| 4.0 |
| Density, g/cm3 | 7.8 | |
| 7.8 |
| Embodied Carbon, kg CO2/kg material | 1.4 | |
| 1.8 |
| Embodied Energy, MJ/kg | 18 | |
| 24 |
| Embodied Water, L/kg | 46 | |
| 60 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 75 to 99 | |
| 110 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 370 to 1090 | |
| 760 |
| Stiffness to Weight: Axial, points | 13 | |
| 13 |
| Stiffness to Weight: Bending, points | 24 | |
| 24 |
| Strength to Weight: Axial, points | 24 to 27 | |
| 22 |
| Strength to Weight: Bending, points | 22 to 23 | |
| 21 |
| Thermal Diffusivity, mm2/s | 14 | |
| 11 |
| Thermal Shock Resistance, points | 22 to 24 | |
| 18 |
Alloy Composition
| Carbon (C), % | 0.46 to 0.53 | |
| 0 to 0.050 |
| Chromium (Cr), % | 0 | |
| 2.0 to 2.5 |
| Copper (Cu), % | 0 | |
| 0 to 0.35 |
| Iron (Fe), % | 98.5 to 98.9 | |
| 93.5 to 96.5 |
| Manganese (Mn), % | 0.6 to 0.9 | |
| 0.4 to 1.0 |
| Molybdenum (Mo), % | 0 | |
| 0.9 to 1.2 |
| Nickel (Ni), % | 0 | |
| 0 to 0.2 |
| Phosphorus (P), % | 0 to 0.040 | |
| 0 to 0.025 |
| Silicon (Si), % | 0 | |
| 0.25 to 0.6 |
| Sulfur (S), % | 0 to 0.050 | |
| 0 to 0.030 |
| Vanadium (V), % | 0 | |
| 0 to 0.030 |
| Residuals, % | 0 | |
| 0 to 0.5 |