SAE-AISI 1050 Steel vs. C94100 Bronze
SAE-AISI 1050 steel belongs to the iron alloys classification, while C94100 bronze belongs to the copper alloys. There are 26 material properties with values for both materials. Properties with values for just one material (6, in this case) are not shown.
For each property being compared, the top bar is SAE-AISI 1050 steel and the bottom bar is C94100 bronze.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 190 | |
| 92 |
| Elongation at Break, % | 11 to 17 | |
| 7.8 |
| Poisson's Ratio | 0.29 | |
| 0.36 |
| Shear Modulus, GPa | 72 | |
| 34 |
| Tensile Strength: Ultimate (UTS), MPa | 690 to 790 | |
| 190 |
| Tensile Strength: Yield (Proof), MPa | 390 to 650 | |
| 130 |
Thermal Properties
| Latent Heat of Fusion, J/g | 250 | |
| 160 |
| Maximum Temperature: Mechanical, °C | 400 | |
| 130 |
| Melting Completion (Liquidus), °C | 1460 | |
| 870 |
| Melting Onset (Solidus), °C | 1420 | |
| 790 |
| Specific Heat Capacity, J/kg-K | 470 | |
| 330 |
| Thermal Expansion, µm/m-K | 12 | |
| 20 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 7.0 | |
| 9.0 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 8.1 | |
| 8.8 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 1.8 | |
| 29 |
| Density, g/cm3 | 7.8 | |
| 9.2 |
| Embodied Carbon, kg CO2/kg material | 1.4 | |
| 3.0 |
| Embodied Energy, MJ/kg | 18 | |
| 48 |
| Embodied Water, L/kg | 46 | |
| 370 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 81 to 100 | |
| 14 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 400 to 1130 | |
| 97 |
| Stiffness to Weight: Axial, points | 13 | |
| 5.5 |
| Stiffness to Weight: Bending, points | 24 | |
| 16 |
| Strength to Weight: Axial, points | 25 to 28 | |
| 5.8 |
| Strength to Weight: Bending, points | 22 to 24 | |
| 8.1 |
| Thermal Shock Resistance, points | 22 to 25 | |
| 7.6 |
Alloy Composition
| Aluminum (Al), % | 0 | |
| 0 to 0.0050 |
| Antimony (Sb), % | 0 | |
| 0 to 0.8 |
| Carbon (C), % | 0.48 to 0.55 | |
| 0 |
| Copper (Cu), % | 0 | |
| 72 to 79 |
| Iron (Fe), % | 98.5 to 98.9 | |
| 0 to 0.25 |
| Lead (Pb), % | 0 | |
| 18 to 22 |
| Manganese (Mn), % | 0.6 to 0.9 | |
| 0 |
| Nickel (Ni), % | 0 | |
| 0 to 1.0 |
| Phosphorus (P), % | 0 to 0.040 | |
| 0 to 1.5 |
| Silicon (Si), % | 0 | |
| 0 to 0.0050 |
| Sulfur (S), % | 0 to 0.050 | |
| 0 to 0.080 |
| Tin (Sn), % | 0 | |
| 4.5 to 6.5 |
| Zinc (Zn), % | 0 | |
| 0 to 1.0 |
| Residuals, % | 0 | |
| 0 to 1.3 |