SAE-AISI 1090 Steel vs. N06045 Nickel
SAE-AISI 1090 steel belongs to the iron alloys classification, while N06045 nickel belongs to the nickel alloys. They have a modest 24% of their average alloy composition in common, which, by itself, doesn't mean much. There are 26 material properties with values for both materials. Properties with values for just one material (7, in this case) are not shown.
For each property being compared, the top bar is SAE-AISI 1090 steel and the bottom bar is N06045 nickel.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 190 | |
| 200 |
| Elongation at Break, % | 11 | |
| 37 |
| Fatigue Strength, MPa | 320 to 380 | |
| 210 |
| Poisson's Ratio | 0.29 | |
| 0.28 |
| Shear Modulus, GPa | 72 | |
| 77 |
| Shear Strength, MPa | 470 to 570 | |
| 470 |
| Tensile Strength: Ultimate (UTS), MPa | 790 to 950 | |
| 690 |
| Tensile Strength: Yield (Proof), MPa | 520 to 610 | |
| 270 |
Thermal Properties
| Latent Heat of Fusion, J/g | 240 | |
| 350 |
| Maximum Temperature: Mechanical, °C | 400 | |
| 1010 |
| Melting Completion (Liquidus), °C | 1450 | |
| 1350 |
| Melting Onset (Solidus), °C | 1410 | |
| 1300 |
| Specific Heat Capacity, J/kg-K | 470 | |
| 480 |
| Thermal Expansion, µm/m-K | 12 | |
| 13 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 1.8 | |
| 42 |
| Density, g/cm3 | 7.8 | |
| 8.0 |
| Embodied Carbon, kg CO2/kg material | 1.4 | |
| 6.9 |
| Embodied Energy, MJ/kg | 19 | |
| 98 |
| Embodied Water, L/kg | 46 | |
| 250 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 82 to 91 | |
| 200 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 730 to 1000 | |
| 180 |
| Stiffness to Weight: Axial, points | 13 | |
| 14 |
| Stiffness to Weight: Bending, points | 24 | |
| 24 |
| Strength to Weight: Axial, points | 28 to 34 | |
| 24 |
| Strength to Weight: Bending, points | 24 to 27 | |
| 22 |
| Thermal Shock Resistance, points | 25 to 31 | |
| 18 |
Alloy Composition
| Carbon (C), % | 0.85 to 1.0 | |
| 0.050 to 0.12 |
| Cerium (Ce), % | 0 | |
| 0.030 to 0.090 |
| Chromium (Cr), % | 0 | |
| 26 to 29 |
| Copper (Cu), % | 0 | |
| 0 to 0.3 |
| Iron (Fe), % | 98 to 98.6 | |
| 21 to 25 |
| Manganese (Mn), % | 0.6 to 0.9 | |
| 0 to 1.0 |
| Nickel (Ni), % | 0 | |
| 45 to 50.4 |
| Phosphorus (P), % | 0 to 0.040 | |
| 0 to 0.020 |
| Silicon (Si), % | 0 | |
| 2.5 to 3.0 |
| Sulfur (S), % | 0 to 0.050 | |
| 0 to 0.010 |