SAE-AISI 1090 Steel vs. N07041 Nickel
SAE-AISI 1090 steel belongs to the iron alloys classification, while N07041 nickel belongs to the nickel alloys. There are 19 material properties with values for both materials. Properties with values for just one material (13, in this case) are not shown.
For each property being compared, the top bar is SAE-AISI 1090 steel and the bottom bar is N07041 nickel.
Metric UnitsUS Customary Units
Mechanical Properties
Elastic (Young's, Tensile) Modulus, GPa | 190 | |
220 |
Elongation at Break, % | 11 | |
14 |
Fatigue Strength, MPa | 320 to 380 | |
540 |
Shear Strength, MPa | 470 to 570 | |
850 |
Tensile Strength: Ultimate (UTS), MPa | 790 to 950 | |
1400 |
Tensile Strength: Yield (Proof), MPa | 520 to 610 | |
1050 |
Thermal Properties
Melting Onset (Solidus), °C | 1410 | |
1320 |
Specific Heat Capacity, J/kg-K | 470 | |
450 |
Thermal Conductivity, W/m-K | 50 | |
11 |
Thermal Expansion, µm/m-K | 12 | |
12 |
Otherwise Unclassified Properties
Density, g/cm3 | 7.8 | |
8.2 |
Common Calculations
Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 82 to 91 | |
180 |
Resilience: Unit (Modulus of Resilience), kJ/m3 | 730 to 1000 | |
2510 |
Stiffness to Weight: Axial, points | 13 | |
15 |
Stiffness to Weight: Bending, points | 24 | |
25 |
Strength to Weight: Axial, points | 28 to 34 | |
47 |
Strength to Weight: Bending, points | 24 to 27 | |
34 |
Thermal Diffusivity, mm2/s | 13 | |
3.0 |
Thermal Shock Resistance, points | 25 to 31 | |
38 |