SAE-AISI 1140 Steel vs. EN 1.1181 Steel
Both SAE-AISI 1140 steel and EN 1.1181 steel are iron alloys. Their average alloy composition is basically identical. There are 31 material properties with values for both materials. Properties with values for just one material (2, in this case) are not shown.
For each property being compared, the top bar is SAE-AISI 1140 steel and the bottom bar is EN 1.1181 steel.
Metric UnitsUS Customary Units
Mechanical Properties
| Brinell Hardness | 170 to 180 | |
| 160 to 180 |
| Elastic (Young's, Tensile) Modulus, GPa | 190 | |
| 190 |
| Elongation at Break, % | 14 to 18 | |
| 19 to 20 |
| Fatigue Strength, MPa | 230 to 370 | |
| 190 to 260 |
| Poisson's Ratio | 0.29 | |
| 0.29 |
| Shear Modulus, GPa | 72 | |
| 73 |
| Shear Strength, MPa | 370 to 420 | |
| 350 to 390 |
| Tensile Strength: Ultimate (UTS), MPa | 600 to 700 | |
| 560 to 620 |
| Tensile Strength: Yield (Proof), MPa | 340 to 570 | |
| 280 to 380 |
Thermal Properties
| Latent Heat of Fusion, J/g | 250 | |
| 250 |
| Maximum Temperature: Mechanical, °C | 400 | |
| 400 |
| Melting Completion (Liquidus), °C | 1460 | |
| 1460 |
| Melting Onset (Solidus), °C | 1420 | |
| 1420 |
| Specific Heat Capacity, J/kg-K | 470 | |
| 470 |
| Thermal Conductivity, W/m-K | 51 | |
| 42 |
| Thermal Expansion, µm/m-K | 13 | |
| 11 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 7.0 | |
| 7.2 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 8.1 | |
| 8.3 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 1.8 | |
| 2.1 |
| Density, g/cm3 | 7.8 | |
| 7.8 |
| Embodied Carbon, kg CO2/kg material | 1.4 | |
| 1.4 |
| Embodied Energy, MJ/kg | 18 | |
| 19 |
| Embodied Water, L/kg | 46 | |
| 47 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 89 to 93 | |
| 90 to 110 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 310 to 870 | |
| 210 to 380 |
| Stiffness to Weight: Axial, points | 13 | |
| 13 |
| Stiffness to Weight: Bending, points | 24 | |
| 24 |
| Strength to Weight: Axial, points | 21 to 25 | |
| 20 to 22 |
| Strength to Weight: Bending, points | 20 to 22 | |
| 19 to 21 |
| Thermal Diffusivity, mm2/s | 14 | |
| 11 |
| Thermal Shock Resistance, points | 18 to 21 | |
| 19 to 21 |
Alloy Composition
| Carbon (C), % | 0.37 to 0.44 | |
| 0.32 to 0.39 |
| Chromium (Cr), % | 0 | |
| 0 to 0.4 |
| Iron (Fe), % | 98.4 to 98.9 | |
| 97.4 to 99.18 |
| Manganese (Mn), % | 0.7 to 1.0 | |
| 0.5 to 0.8 |
| Molybdenum (Mo), % | 0 | |
| 0 to 0.1 |
| Nickel (Ni), % | 0 | |
| 0 to 0.4 |
| Phosphorus (P), % | 0 to 0.040 | |
| 0 to 0.035 |
| Silicon (Si), % | 0 | |
| 0 to 0.4 |
| Sulfur (S), % | 0.080 to 0.13 | |
| 0 to 0.035 |