SAE-AISI 9310 Steel vs. SAE-AISI 1345 Steel
Both SAE-AISI 9310 steel and SAE-AISI 1345 steel are iron alloys. They have a very high 95% of their average alloy composition in common. There are 31 material properties with values for both materials. Properties with values for just one material (1, in this case) are not shown.
For each property being compared, the top bar is SAE-AISI 9310 steel and the bottom bar is SAE-AISI 1345 steel.
Metric UnitsUS Customary Units
Mechanical Properties
| Brinell Hardness | 540 to 610 | |
| 170 to 210 |
| Elastic (Young's, Tensile) Modulus, GPa | 190 | |
| 190 |
| Elongation at Break, % | 17 to 19 | |
| 11 to 23 |
| Fatigue Strength, MPa | 300 to 390 | |
| 230 to 390 |
| Poisson's Ratio | 0.29 | |
| 0.29 |
| Shear Modulus, GPa | 73 | |
| 72 |
| Shear Strength, MPa | 510 to 570 | |
| 370 to 440 |
| Tensile Strength: Ultimate (UTS), MPa | 820 to 910 | |
| 590 to 730 |
| Tensile Strength: Yield (Proof), MPa | 450 to 570 | |
| 330 to 620 |
Thermal Properties
| Latent Heat of Fusion, J/g | 250 | |
| 250 |
| Maximum Temperature: Mechanical, °C | 440 | |
| 400 |
| Melting Completion (Liquidus), °C | 1460 | |
| 1450 |
| Melting Onset (Solidus), °C | 1420 | |
| 1410 |
| Specific Heat Capacity, J/kg-K | 470 | |
| 470 |
| Thermal Conductivity, W/m-K | 48 | |
| 51 |
| Thermal Expansion, µm/m-K | 13 | |
| 12 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 7.7 | |
| 7.2 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 8.9 | |
| 8.3 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 4.4 | |
| 1.9 |
| Density, g/cm3 | 7.9 | |
| 7.8 |
| Embodied Carbon, kg CO2/kg material | 1.8 | |
| 1.4 |
| Embodied Energy, MJ/kg | 24 | |
| 19 |
| Embodied Water, L/kg | 57 | |
| 48 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 120 to 150 | |
| 78 to 120 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 540 to 860 | |
| 290 to 1040 |
| Stiffness to Weight: Axial, points | 13 | |
| 13 |
| Stiffness to Weight: Bending, points | 24 | |
| 24 |
| Strength to Weight: Axial, points | 29 to 32 | |
| 21 to 26 |
| Strength to Weight: Bending, points | 25 to 27 | |
| 20 to 23 |
| Thermal Diffusivity, mm2/s | 13 | |
| 14 |
| Thermal Shock Resistance, points | 24 to 27 | |
| 19 to 23 |
Alloy Composition
| Carbon (C), % | 0.080 to 0.13 | |
| 0.43 to 0.48 |
| Chromium (Cr), % | 1.0 to 1.4 | |
| 0 |
| Iron (Fe), % | 93.8 to 95.2 | |
| 97.2 to 97.8 |
| Manganese (Mn), % | 0.45 to 0.65 | |
| 1.6 to 1.9 |
| Molybdenum (Mo), % | 0.080 to 0.15 | |
| 0 |
| Nickel (Ni), % | 3.0 to 3.5 | |
| 0 |
| Phosphorus (P), % | 0 to 0.015 | |
| 0 to 0.035 |
| Silicon (Si), % | 0.2 to 0.35 | |
| 0.15 to 0.35 |
| Sulfur (S), % | 0 to 0.012 | |
| 0 to 0.040 |