SAE-AISI D7 Steel vs. Grade 364 Molybdenum

SAE-AISI D7 steel belongs to the iron alloys classification, while grade 364 molybdenum belongs to the otherwise unclassified metals. There are 16 material properties with values for both materials. Properties with values for just one material (10, in this case) are not shown.

For each property being compared, the top bar is SAE-AISI D7 steel and the bottom bar is grade 364 molybdenum.

SAE-AISI D7 (T30407) Chromium Cold-Work Steel Grade 364 Molybdenum

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa		190
Elastic (Young's, Tensile) Modulus, GPa		310

Poisson's Ratio		0.28
Poisson's Ratio		0.31

Shear Modulus, GPa		73
Shear Modulus, GPa		120

Tensile Strength: Ultimate (UTS), MPa		800 to 2120
Tensile Strength: Ultimate (UTS), MPa		580 to 720

Thermal Properties

Latent Heat of Fusion, J/g		270
Latent Heat of Fusion, J/g		370

Specific Heat Capacity, J/kg-K		480
Specific Heat Capacity, J/kg-K		250

Thermal Expansion, µm/m-K		11
Thermal Expansion, µm/m-K		7.0

Otherwise Unclassified Properties

Density, g/cm³		7.6
Density, g/cm³		10

Embodied Carbon, kg CO₂/kg material		11
Embodied Carbon, kg CO₂/kg material		28

Embodied Energy, MJ/kg		180
Embodied Energy, MJ/kg		330

Embodied Water, L/kg		130
Embodied Water, L/kg		360

Common Calculations

Stiffness to Weight: Axial, points		14
Stiffness to Weight: Axial, points		17

Stiffness to Weight: Bending, points		25
Stiffness to Weight: Bending, points		22

Strength to Weight: Axial, points		29 to 78
Strength to Weight: Axial, points		16 to 20

Strength to Weight: Bending, points		25 to 48
Strength to Weight: Bending, points		15 to 17

Thermal Shock Resistance, points		27 to 72
Thermal Shock Resistance, points		19 to 24

Alloy Composition

Carbon (C), %		2.2 to 2.5
Carbon (C), %		0.010 to 0.040

Chromium (Cr), %		11.5 to 13.5
Chromium (Cr), %		0

Copper (Cu), %		0 to 0.25
Copper (Cu), %		0

Iron (Fe), %		76.6 to 81.9
Iron (Fe), %		0 to 0.010

Manganese (Mn), %		0 to 0.6
Manganese (Mn), %		0

Molybdenum (Mo), %		0.7 to 1.2
Molybdenum (Mo), %		99.2 to 99.5

Nickel (Ni), %		0 to 0.3
Nickel (Ni), %		0 to 0.0050

Nitrogen (N), %		0
Nitrogen (N), %		0 to 0.0020

Oxygen (O), %		0
Oxygen (O), %		0 to 0.030

Phosphorus (P), %		0 to 0.030
Phosphorus (P), %		0

Silicon (Si), %		0 to 0.6
Silicon (Si), %		0 to 0.0050

Sulfur (S), %		0 to 0.030
Sulfur (S), %		0

Titanium (Ti), %		0
Titanium (Ti), %		0.4 to 0.55

Vanadium (V), %		3.8 to 4.4
Vanadium (V), %		0

Zirconium (Zr), %		0
Zirconium (Zr), %		0.060 to 0.12