SAE-AISI M43 Steel vs. EN 1.4724 Stainless Steel

Both SAE-AISI M43 steel and EN 1.4724 stainless steel are iron alloys. They have 78% of their average alloy composition in common. There are 22 material properties with values for both materials. Properties with values for just one material (11, in this case) are not shown.

For each property being compared, the top bar is SAE-AISI M43 steel and the bottom bar is EN 1.4724 stainless steel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 200
190
Poisson's Ratio 0.29
0.28
Shear Modulus, GPa 77
75
Tensile Strength: Ultimate (UTS), MPa 810 to 2290
550

Thermal Properties

Latent Heat of Fusion, J/g 270
290
Melting Completion (Liquidus), °C 1550
1430
Melting Onset (Solidus), °C 1500
1390
Specific Heat Capacity, J/kg-K 450
490
Thermal Conductivity, W/m-K 19
21
Thermal Expansion, µm/m-K 12
11

Otherwise Unclassified Properties

Base Metal Price, % relative 33
7.0
Density, g/cm3 8.2
7.7
Embodied Carbon, kg CO2/kg material 8.5
2.0
Embodied Energy, MJ/kg 120
28
Embodied Water, L/kg 140
110

Common Calculations

PREN (Pitting Resistance) 35
13
Stiffness to Weight: Axial, points 14
14
Stiffness to Weight: Bending, points 24
25
Strength to Weight: Axial, points 27 to 77
20
Strength to Weight: Bending, points 24 to 47
19
Thermal Diffusivity, mm2/s 5.3
5.6
Thermal Shock Resistance, points 25 to 71
19

Alloy Composition

Aluminum (Al), % 0
0.7 to 1.2
Carbon (C), % 1.2 to 1.3
0 to 0.12
Chromium (Cr), % 3.5 to 4.3
12 to 14
Cobalt (Co), % 7.8 to 8.8
0
Copper (Cu), % 0 to 0.25
0
Iron (Fe), % 70.8 to 76
82.2 to 86.6
Manganese (Mn), % 0.2 to 0.4
0 to 1.0
Molybdenum (Mo), % 7.5 to 8.5
0
Nickel (Ni), % 0 to 0.3
0
Phosphorus (P), % 0 to 0.030
0 to 0.040
Silicon (Si), % 0.15 to 0.65
0.7 to 1.4
Sulfur (S), % 0 to 0.030
0 to 0.015
Tungsten (W), % 2.3 to 3.0
0
Vanadium (V), % 1.5 to 1.8
0