SAE-AISI O2 Steel vs. C11600 Copper
SAE-AISI O2 steel belongs to the iron alloys classification, while C11600 copper belongs to the copper alloys. There are 23 material properties with values for both materials. Properties with values for just one material (8, in this case) are not shown.
For each property being compared, the top bar is SAE-AISI O2 steel and the bottom bar is C11600 copper.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 190 | |
| 120 |
| Poisson's Ratio | 0.29 | |
| 0.34 |
| Shear Modulus, GPa | 72 | |
| 43 |
| Tensile Strength: Ultimate (UTS), MPa | 640 to 2050 | |
| 230 to 410 |
Thermal Properties
| Latent Heat of Fusion, J/g | 250 | |
| 210 |
| Melting Completion (Liquidus), °C | 1450 | |
| 1080 |
| Melting Onset (Solidus), °C | 1410 | |
| 1030 |
| Specific Heat Capacity, J/kg-K | 470 | |
| 390 |
| Thermal Conductivity, W/m-K | 43 | |
| 390 |
| Thermal Expansion, µm/m-K | 11 | |
| 17 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 7.4 | |
| 100 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 8.6 | |
| 100 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 2.4 | |
| 35 |
| Density, g/cm3 | 7.8 | |
| 9.0 |
| Embodied Carbon, kg CO2/kg material | 1.8 | |
| 2.7 |
| Embodied Energy, MJ/kg | 26 | |
| 42 |
| Embodied Water, L/kg | 50 | |
| 390 |
Common Calculations
| Stiffness to Weight: Axial, points | 13 | |
| 7.2 |
| Stiffness to Weight: Bending, points | 24 | |
| 18 |
| Strength to Weight: Axial, points | 23 to 73 | |
| 7.2 to 13 |
| Strength to Weight: Bending, points | 21 to 46 | |
| 9.4 to 14 |
| Thermal Diffusivity, mm2/s | 12 | |
| 110 |
| Thermal Shock Resistance, points | 22 to 70 | |
| 8.2 to 15 |
Alloy Composition
| Carbon (C), % | 0.85 to 1.0 | |
| 0 |
| Chromium (Cr), % | 0 to 0.5 | |
| 0 |
| Copper (Cu), % | 0 to 0.25 | |
| 99.78 to 99.915 |
| Iron (Fe), % | 95 to 97.8 | |
| 0 |
| Manganese (Mn), % | 1.4 to 1.8 | |
| 0 |
| Molybdenum (Mo), % | 0 to 0.3 | |
| 0 |
| Nickel (Ni), % | 0 to 0.3 | |
| 0 |
| Phosphorus (P), % | 0 to 0.030 | |
| 0 |
| Silicon (Si), % | 0 to 0.5 | |
| 0 |
| Silver (Ag), % | 0 | |
| 0.085 to 0.12 |
| Sulfur (S), % | 0 to 0.030 | |
| 0 |
| Vanadium (V), % | 0 to 0.3 | |
| 0 |
| Residuals, % | 0 | |
| 0 to 0.1 |