SAE-AISI O6 Steel vs. EN 1.4011 Stainless Steel

Both SAE-AISI O6 steel and EN 1.4011 stainless steel are iron alloys. They have 87% of their average alloy composition in common. There are 23 material properties with values for both materials. Properties with values for just one material (9, in this case) are not shown.

For each property being compared, the top bar is SAE-AISI O6 steel and the bottom bar is EN 1.4011 stainless steel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 180
190
Poisson's Ratio 0.29
0.28
Shear Modulus, GPa 71
76
Tensile Strength: Ultimate (UTS), MPa 670 to 2070
700

Thermal Properties

Latent Heat of Fusion, J/g 260
270
Melting Completion (Liquidus), °C 1430
1450
Melting Onset (Solidus), °C 1390
1400
Specific Heat Capacity, J/kg-K 480
480
Thermal Conductivity, W/m-K 43
25
Thermal Expansion, µm/m-K 12
11

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 7.4
2.9
Electrical Conductivity: Equal Weight (Specific), % IACS 8.6
3.4

Otherwise Unclassified Properties

Base Metal Price, % relative 2.3
7.0
Density, g/cm3 7.7
7.8
Embodied Carbon, kg CO2/kg material 1.5
2.0
Embodied Energy, MJ/kg 21
28
Embodied Water, L/kg 47
100

Common Calculations

Stiffness to Weight: Axial, points 13
14
Stiffness to Weight: Bending, points 25
25
Strength to Weight: Axial, points 24 to 74
25
Strength to Weight: Bending, points 22 to 47
23
Thermal Diffusivity, mm2/s 12
6.7
Thermal Shock Resistance, points 22 to 69
24

Alloy Composition

Carbon (C), % 1.3 to 1.6
0 to 0.15
Chromium (Cr), % 0 to 0.3
11.5 to 13.5
Copper (Cu), % 0 to 0.25
0
Iron (Fe), % 94.6 to 97.7
82.8 to 88.5
Manganese (Mn), % 0.3 to 1.1
0 to 1.0
Molybdenum (Mo), % 0.2 to 0.3
0 to 0.5
Nickel (Ni), % 0 to 0.3
0 to 1.0
Phosphorus (P), % 0 to 0.030
0 to 0.035
Silicon (Si), % 0.55 to 1.5
0 to 1.0
Sulfur (S), % 0 to 0.030
0 to 0.025