SAE-AISI P2 Steel vs. AWS E307

Both SAE-AISI P2 steel and AWS E307 are iron alloys. They have 67% of their average alloy composition in common. There are 23 material properties with values for both materials. Properties with values for just one material (2, in this case) are not shown.

For each property being compared, the top bar is SAE-AISI P2 steel and the bottom bar is AWS E307.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 190
200
Poisson's Ratio 0.29
0.28
Shear Modulus, GPa 73
78
Tensile Strength: Ultimate (UTS), MPa 330 to 1980
660

Thermal Properties

Latent Heat of Fusion, J/g 250
290
Melting Completion (Liquidus), °C 1460
1420
Melting Onset (Solidus), °C 1420
1370
Specific Heat Capacity, J/kg-K 470
480
Thermal Conductivity, W/m-K 46
15
Thermal Expansion, µm/m-K 12
14

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 7.3
2.1
Electrical Conductivity: Equal Weight (Specific), % IACS 8.3
2.4

Otherwise Unclassified Properties

Base Metal Price, % relative 2.7
17
Density, g/cm3 7.9
7.8
Embodied Carbon, kg CO2/kg material 1.5
3.5
Embodied Energy, MJ/kg 20
49
Embodied Water, L/kg 51
160

Common Calculations

Stiffness to Weight: Axial, points 13
14
Stiffness to Weight: Bending, points 24
25
Strength to Weight: Axial, points 12 to 70
24
Strength to Weight: Bending, points 14 to 45
22
Thermal Diffusivity, mm2/s 12
4.1
Thermal Shock Resistance, points 11 to 65
17

Alloy Composition

Carbon (C), % 0 to 0.1
0.040 to 0.14
Chromium (Cr), % 0.75 to 1.3
18 to 21.5
Copper (Cu), % 0 to 0.25
0 to 0.75
Iron (Fe), % 96.6 to 98.8
59.6 to 69.2
Manganese (Mn), % 0.1 to 0.4
3.3 to 4.8
Molybdenum (Mo), % 0.15 to 0.4
0.5 to 1.5
Nickel (Ni), % 0.1 to 0.5
9.0 to 10.7
Phosphorus (P), % 0 to 0.030
0 to 0.040
Silicon (Si), % 0.1 to 0.4
0 to 1.0
Sulfur (S), % 0 to 0.030
0 to 0.030