SAE-AISI S7 Steel vs. N06035 Nickel

SAE-AISI S7 steel belongs to the iron alloys classification, while N06035 nickel belongs to the nickel alloys. There are 19 material properties with values for both materials. Properties with values for just one material (12, in this case) are not shown.

For each property being compared, the top bar is SAE-AISI S7 steel and the bottom bar is N06035 nickel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 190
210
Poisson's Ratio 0.29
0.28
Shear Modulus, GPa 74
84
Tensile Strength: Ultimate (UTS), MPa 670 to 2030
660

Thermal Properties

Latent Heat of Fusion, J/g 260
340
Melting Completion (Liquidus), °C 1460
1440
Melting Onset (Solidus), °C 1420
1390
Specific Heat Capacity, J/kg-K 470
450
Thermal Expansion, µm/m-K 12
13

Otherwise Unclassified Properties

Base Metal Price, % relative 5.0
60
Density, g/cm3 7.8
8.4
Embodied Carbon, kg CO2/kg material 2.3
10
Embodied Energy, MJ/kg 31
140
Embodied Water, L/kg 65
330

Common Calculations

Stiffness to Weight: Axial, points 14
14
Stiffness to Weight: Bending, points 25
24
Strength to Weight: Axial, points 24 to 72
22
Strength to Weight: Bending, points 22 to 46
20
Thermal Shock Resistance, points 22 to 66
17

Alloy Composition

Aluminum (Al), % 0
0 to 0.4
Carbon (C), % 0.45 to 0.55
0 to 0.050
Chromium (Cr), % 3.0 to 3.5
32.3 to 34.3
Cobalt (Co), % 0
0 to 1.0
Copper (Cu), % 0 to 0.25
0 to 0.3
Iron (Fe), % 91.6 to 94.9
0 to 2.0
Manganese (Mn), % 0.2 to 0.9
0 to 0.5
Molybdenum (Mo), % 1.3 to 1.8
7.6 to 9.0
Nickel (Ni), % 0
51.1 to 60.2
Phosphorus (P), % 0 to 0.030
0 to 0.030
Silicon (Si), % 0.2 to 1.0
0 to 0.6
Sulfur (S), % 0 to 0.030
0 to 0.015
Tungsten (W), % 0
0 to 0.6
Vanadium (V), % 0 to 0.3
0 to 0.2