MakeItFrom.com
Menu (ESC)

SAE-AISI T1 Steel vs. EN 2.4668 Nickel

SAE-AISI T1 steel belongs to the iron alloys classification, while EN 2.4668 nickel belongs to the nickel alloys. They have a modest 23% of their average alloy composition in common, which, by itself, doesn't mean much. There are 21 material properties with values for both materials. Properties with values for just one material (11, in this case) are not shown.

For each property being compared, the top bar is SAE-AISI T1 steel and the bottom bar is EN 2.4668 nickel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 200
190
Poisson's Ratio 0.29
0.29
Shear Modulus, GPa 80
75
Tensile Strength: Ultimate (UTS), MPa 770 to 2130
1390

Thermal Properties

Latent Heat of Fusion, J/g 240
310
Melting Completion (Liquidus), °C 1810
1460
Melting Onset (Solidus), °C 1750
1410
Specific Heat Capacity, J/kg-K 410
450
Thermal Conductivity, W/m-K 20
13
Thermal Expansion, µm/m-K 12
13

Otherwise Unclassified Properties

Base Metal Price, % relative 45
75
Density, g/cm3 9.3
8.3
Embodied Carbon, kg CO2/kg material 8.2
13
Embodied Energy, MJ/kg 130
190
Embodied Water, L/kg 90
250

Common Calculations

Stiffness to Weight: Axial, points 12
13
Stiffness to Weight: Bending, points 21
23
Strength to Weight: Axial, points 23 to 64
46
Strength to Weight: Bending, points 20 to 40
33
Thermal Diffusivity, mm2/s 5.2
3.5
Thermal Shock Resistance, points 23 to 64
40

Alloy Composition

Aluminum (Al), % 0
0.3 to 0.7
Boron (B), % 0
0.0020 to 0.0060
Carbon (C), % 0.65 to 0.8
0.020 to 0.080
Chromium (Cr), % 3.8 to 4.5
17 to 21
Cobalt (Co), % 0
0 to 1.0
Copper (Cu), % 0 to 0.25
0 to 0.3
Iron (Fe), % 73.2 to 77.2
11.2 to 24.6
Manganese (Mn), % 0.1 to 0.4
0 to 0.35
Molybdenum (Mo), % 0
2.8 to 3.3
Nickel (Ni), % 0 to 0.3
50 to 55
Niobium (Nb), % 0
4.7 to 5.5
Phosphorus (P), % 0 to 0.030
0 to 0.015
Silicon (Si), % 0.2 to 0.4
0 to 0.35
Sulfur (S), % 0 to 0.030
0 to 0.015
Titanium (Ti), % 0
0.6 to 1.2
Tungsten (W), % 17.3 to 18.8
0
Vanadium (V), % 0.9 to 1.3
0