SAE-AISI T1 Steel vs. N06058 Nickel

SAE-AISI T1 steel belongs to the iron alloys classification, while N06058 nickel belongs to the nickel alloys. There are 21 material properties with values for both materials. Properties with values for just one material (8, in this case) are not shown.

For each property being compared, the top bar is SAE-AISI T1 steel and the bottom bar is N06058 nickel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 200
220
Poisson's Ratio 0.29
0.29
Shear Modulus, GPa 80
86
Tensile Strength: Ultimate (UTS), MPa 770 to 2130
860

Thermal Properties

Latent Heat of Fusion, J/g 240
330
Melting Completion (Liquidus), °C 1810
1540
Melting Onset (Solidus), °C 1750
1490
Specific Heat Capacity, J/kg-K 410
420
Thermal Conductivity, W/m-K 20
9.8
Thermal Expansion, µm/m-K 12
12

Otherwise Unclassified Properties

Base Metal Price, % relative 45
70
Density, g/cm3 9.3
8.8
Embodied Carbon, kg CO2/kg material 8.2
13
Embodied Energy, MJ/kg 130
170
Embodied Water, L/kg 90
310

Common Calculations

Stiffness to Weight: Axial, points 12
14
Stiffness to Weight: Bending, points 21
23
Strength to Weight: Axial, points 23 to 64
27
Strength to Weight: Bending, points 20 to 40
23
Thermal Diffusivity, mm2/s 5.2
2.6
Thermal Shock Resistance, points 23 to 64
23

Alloy Composition

Aluminum (Al), % 0
0 to 0.4
Carbon (C), % 0.65 to 0.8
0 to 0.010
Chromium (Cr), % 3.8 to 4.5
20 to 23
Cobalt (Co), % 0
0 to 0.3
Copper (Cu), % 0 to 0.25
0 to 0.5
Iron (Fe), % 73.2 to 77.2
0 to 1.5
Manganese (Mn), % 0.1 to 0.4
0 to 0.5
Molybdenum (Mo), % 0
19 to 21
Nickel (Ni), % 0 to 0.3
52.2 to 61
Nitrogen (N), % 0
0.020 to 0.15
Phosphorus (P), % 0 to 0.030
0 to 0.015
Silicon (Si), % 0.2 to 0.4
0 to 0.1
Sulfur (S), % 0 to 0.030
0 to 0.010
Tungsten (W), % 17.3 to 18.8
0 to 0.3
Vanadium (V), % 0.9 to 1.3
0