C11400 Copper vs. N08904 Stainless Steel
C11400 copper belongs to the copper alloys classification, while N08904 stainless steel belongs to the iron alloys. There are 30 material properties with values for both materials. Properties with values for just one material (6, in this case) are not shown.
For each property being compared, the top bar is C11400 copper and the bottom bar is N08904 stainless steel.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 120 | |
| 200 |
| Elongation at Break, % | 2.8 to 51 | |
| 38 |
| Poisson's Ratio | 0.34 | |
| 0.28 |
| Rockwell B Hardness | 10 to 62 | |
| 77 |
| Shear Modulus, GPa | 43 | |
| 79 |
| Shear Strength, MPa | 150 to 210 | |
| 370 |
| Tensile Strength: Ultimate (UTS), MPa | 220 to 400 | |
| 540 |
| Tensile Strength: Yield (Proof), MPa | 75 to 400 | |
| 240 |
Thermal Properties
| Latent Heat of Fusion, J/g | 210 | |
| 300 |
| Maximum Temperature: Mechanical, °C | 200 | |
| 1100 |
| Melting Completion (Liquidus), °C | 1080 | |
| 1440 |
| Melting Onset (Solidus), °C | 1030 | |
| 1390 |
| Specific Heat Capacity, J/kg-K | 390 | |
| 470 |
| Thermal Conductivity, W/m-K | 390 | |
| 12 |
| Thermal Expansion, µm/m-K | 17 | |
| 16 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 100 | |
| 1.7 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 100 | |
| 1.9 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 32 | |
| 32 |
| Density, g/cm3 | 9.0 | |
| 8.1 |
| Embodied Carbon, kg CO2/kg material | 2.6 | |
| 5.8 |
| Embodied Energy, MJ/kg | 42 | |
| 79 |
| Embodied Water, L/kg | 350 | |
| 200 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 11 to 90 | |
| 170 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 24 to 680 | |
| 150 |
| Stiffness to Weight: Axial, points | 7.2 | |
| 14 |
| Stiffness to Weight: Bending, points | 18 | |
| 24 |
| Strength to Weight: Axial, points | 6.8 to 12 | |
| 19 |
| Strength to Weight: Bending, points | 9.1 to 14 | |
| 18 |
| Thermal Diffusivity, mm2/s | 110 | |
| 3.1 |
| Thermal Shock Resistance, points | 7.8 to 14 | |
| 12 |
Alloy Composition
| Carbon (C), % | 0 | |
| 0 to 0.020 |
| Chromium (Cr), % | 0 | |
| 19 to 23 |
| Copper (Cu), % | 99.84 to 99.966 | |
| 1.0 to 2.0 |
| Iron (Fe), % | 0 | |
| 38.8 to 53 |
| Manganese (Mn), % | 0 | |
| 0 to 2.0 |
| Molybdenum (Mo), % | 0 | |
| 4.0 to 5.0 |
| Nickel (Ni), % | 0 | |
| 23 to 28 |
| Nitrogen (N), % | 0 | |
| 0 to 0.1 |
| Phosphorus (P), % | 0 | |
| 0 to 0.045 |
| Silicon (Si), % | 0 | |
| 0 to 1.0 |
| Silver (Ag), % | 0.034 to 0.060 | |
| 0 |
| Sulfur (S), % | 0 | |
| 0 to 0.035 |
| Residuals, % | 0 to 0.1 | |
| 0 |