C12000 Copper vs. C28000 Muntz Metal
Both C12000 copper and C28000 Muntz Metal are copper alloys. They have 61% of their average alloy composition in common. There are 29 material properties with values for both materials. Properties with values for just one material (3, in this case) are not shown.
For each property being compared, the top bar is C12000 copper and the bottom bar is C28000 Muntz Metal.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 120 | |
| 100 |
| Elongation at Break, % | 2.8 to 50 | |
| 10 to 45 |
| Poisson's Ratio | 0.34 | |
| 0.31 |
| Shear Modulus, GPa | 43 | |
| 40 |
| Shear Strength, MPa | 160 to 240 | |
| 230 to 330 |
| Tensile Strength: Ultimate (UTS), MPa | 230 to 410 | |
| 330 to 610 |
| Tensile Strength: Yield (Proof), MPa | 77 to 400 | |
| 150 to 370 |
Thermal Properties
| Latent Heat of Fusion, J/g | 210 | |
| 170 |
| Maximum Temperature: Mechanical, °C | 200 | |
| 120 |
| Melting Completion (Liquidus), °C | 1080 | |
| 900 |
| Melting Onset (Solidus), °C | 1080 | |
| 900 |
| Specific Heat Capacity, J/kg-K | 390 | |
| 390 |
| Thermal Conductivity, W/m-K | 390 | |
| 120 |
| Thermal Expansion, µm/m-K | 17 | |
| 21 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 98 | |
| 28 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 98 | |
| 31 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 31 | |
| 23 |
| Density, g/cm3 | 9.0 | |
| 8.0 |
| Embodied Carbon, kg CO2/kg material | 2.6 | |
| 2.7 |
| Embodied Energy, MJ/kg | 41 | |
| 46 |
| Embodied Water, L/kg | 310 | |
| 320 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 10 to 91 | |
| 27 to 240 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 25 to 690 | |
| 110 to 670 |
| Stiffness to Weight: Axial, points | 7.2 | |
| 7.2 |
| Stiffness to Weight: Bending, points | 18 | |
| 20 |
| Strength to Weight: Axial, points | 7.2 to 13 | |
| 11 to 21 |
| Strength to Weight: Bending, points | 9.4 to 14 | |
| 13 to 20 |
| Thermal Diffusivity, mm2/s | 110 | |
| 40 |
| Thermal Shock Resistance, points | 8.2 to 15 | |
| 11 to 20 |
Alloy Composition
| Copper (Cu), % | 99.9 to 99.996 | |
| 59 to 63 |
| Iron (Fe), % | 0 | |
| 0 to 0.070 |
| Lead (Pb), % | 0 | |
| 0 to 0.3 |
| Phosphorus (P), % | 0.0040 to 0.012 | |
| 0 |
| Zinc (Zn), % | 0 | |
| 36.3 to 41 |
| Residuals, % | 0 | |
| 0 to 0.3 |