C12500 Copper vs. ASTM A182 Grade F22V
C12500 copper belongs to the copper alloys classification, while ASTM A182 grade F22V belongs to the iron alloys. There are 29 material properties with values for both materials. Properties with values for just one material (5, in this case) are not shown.
For each property being compared, the top bar is C12500 copper and the bottom bar is ASTM A182 grade F22V.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 120 | |
| 190 |
| Elongation at Break, % | 1.5 to 50 | |
| 21 |
| Poisson's Ratio | 0.34 | |
| 0.29 |
| Shear Modulus, GPa | 43 | |
| 74 |
| Shear Strength, MPa | 150 to 220 | |
| 420 |
| Tensile Strength: Ultimate (UTS), MPa | 220 to 420 | |
| 670 |
| Tensile Strength: Yield (Proof), MPa | 75 to 390 | |
| 460 |
Thermal Properties
| Latent Heat of Fusion, J/g | 210 | |
| 250 |
| Maximum Temperature: Mechanical, °C | 200 | |
| 460 |
| Melting Completion (Liquidus), °C | 1080 | |
| 1470 |
| Melting Onset (Solidus), °C | 1070 | |
| 1430 |
| Specific Heat Capacity, J/kg-K | 390 | |
| 470 |
| Thermal Conductivity, W/m-K | 350 | |
| 39 |
| Thermal Expansion, µm/m-K | 17 | |
| 13 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 92 | |
| 7.6 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 93 | |
| 8.7 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 31 | |
| 4.2 |
| Density, g/cm3 | 8.9 | |
| 7.9 |
| Embodied Carbon, kg CO2/kg material | 2.6 | |
| 2.5 |
| Embodied Energy, MJ/kg | 41 | |
| 35 |
| Embodied Water, L/kg | 310 | |
| 61 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 5.6 to 88 | |
| 120 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 24 to 660 | |
| 570 |
| Stiffness to Weight: Axial, points | 7.2 | |
| 13 |
| Stiffness to Weight: Bending, points | 18 | |
| 24 |
| Strength to Weight: Axial, points | 6.9 to 13 | |
| 24 |
| Strength to Weight: Bending, points | 9.1 to 14 | |
| 22 |
| Thermal Diffusivity, mm2/s | 100 | |
| 11 |
| Thermal Shock Resistance, points | 7.8 to 15 | |
| 19 |
Alloy Composition
| Antimony (Sb), % | 0 to 0.0030 | |
| 0 |
| Arsenic (As), % | 0 to 0.012 | |
| 0 |
| Bismuth (Bi), % | 0 to 0.0030 | |
| 0 |
| Boron (B), % | 0 | |
| 0 to 0.0020 |
| Calcium (Ca), % | 0 | |
| 0 to 0.015 |
| Carbon (C), % | 0 | |
| 0.11 to 0.15 |
| Chromium (Cr), % | 0 | |
| 2.0 to 2.5 |
| Copper (Cu), % | 99.88 to 100 | |
| 0 to 0.2 |
| Iron (Fe), % | 0 | |
| 94.6 to 96.4 |
| Lead (Pb), % | 0 to 0.0040 | |
| 0 |
| Manganese (Mn), % | 0 | |
| 0.3 to 0.6 |
| Molybdenum (Mo), % | 0 | |
| 0.9 to 1.1 |
| Nickel (Ni), % | 0 to 0.050 | |
| 0 to 0.25 |
| Niobium (Nb), % | 0 | |
| 0 to 0.070 |
| Phosphorus (P), % | 0 | |
| 0 to 0.015 |
| Silicon (Si), % | 0 | |
| 0 to 0.1 |
| Sulfur (S), % | 0 | |
| 0 to 0.010 |
| Tellurium (Te), % | 0 to 0.025 | |
| 0 |
| Titanium (Ti), % | 0 | |
| 0 to 0.030 |
| Vanadium (V), % | 0 | |
| 0.25 to 0.35 |
| Residuals, % | 0 to 0.3 | |
| 0 |