C17000 Copper vs. AWS BNi-3
C17000 copper belongs to the copper alloys classification, while AWS BNi-3 belongs to the nickel alloys. There are 18 material properties with values for both materials. Properties with values for just one material (13, in this case) are not shown.
For each property being compared, the top bar is C17000 copper and the bottom bar is AWS BNi-3.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 120 | |
| 170 |
| Poisson's Ratio | 0.33 | |
| 0.31 |
| Shear Modulus, GPa | 45 | |
| 66 |
| Tensile Strength: Ultimate (UTS), MPa | 490 to 1310 | |
| 430 |
Thermal Properties
| Latent Heat of Fusion, J/g | 230 | |
| 350 |
| Melting Completion (Liquidus), °C | 980 | |
| 1040 |
| Melting Onset (Solidus), °C | 870 | |
| 980 |
| Specific Heat Capacity, J/kg-K | 390 | |
| 480 |
| Thermal Expansion, µm/m-K | 17 | |
| 10 |
Otherwise Unclassified Properties
| Density, g/cm3 | 8.8 | |
| 8.3 |
| Embodied Carbon, kg CO2/kg material | 8.7 | |
| 9.9 |
| Embodied Energy, MJ/kg | 140 | |
| 140 |
| Embodied Water, L/kg | 310 | |
| 220 |
Common Calculations
| Stiffness to Weight: Axial, points | 7.6 | |
| 12 |
| Stiffness to Weight: Bending, points | 19 | |
| 22 |
| Strength to Weight: Axial, points | 15 to 41 | |
| 14 |
| Strength to Weight: Bending, points | 16 to 30 | |
| 15 |
| Thermal Shock Resistance, points | 17 to 45 | |
| 17 |
Alloy Composition
| Aluminum (Al), % | 0 to 0.2 | |
| 0 to 0.050 |
| Beryllium (Be), % | 1.6 to 1.8 | |
| 0 |
| Boron (B), % | 0 | |
| 2.8 to 3.5 |
| Carbon (C), % | 0 | |
| 0 to 0.060 |
| Cobalt (Co), % | 0 | |
| 0 to 0.1 |
| Copper (Cu), % | 96.3 to 98.2 | |
| 0 |
| Iron (Fe), % | 0 to 0.4 | |
| 0 to 0.5 |
| Nickel (Ni), % | 0.2 to 0.6 | |
| 90.1 to 93.3 |
| Phosphorus (P), % | 0 | |
| 0 to 0.020 |
| Selenium (Se), % | 0 | |
| 0 to 0.0050 |
| Silicon (Si), % | 0 to 0.2 | |
| 4.0 to 5.0 |
| Sulfur (S), % | 0 | |
| 0 to 0.020 |
| Titanium (Ti), % | 0 | |
| 0 to 0.050 |
| Zirconium (Zr), % | 0 | |
| 0 to 0.050 |
| Residuals, % | 0 | |
| 0 to 0.5 |