C17500 Copper vs. C12500 Copper
Both C17500 copper and C12500 copper are copper alloys. They have a very high 97% of their average alloy composition in common. There are 29 material properties with values for both materials. Properties with values for just one material (3, in this case) are not shown.
For each property being compared, the top bar is C17500 copper and the bottom bar is C12500 copper.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 120 | |
| 120 |
| Elongation at Break, % | 6.0 to 30 | |
| 1.5 to 50 |
| Poisson's Ratio | 0.34 | |
| 0.34 |
| Shear Modulus, GPa | 45 | |
| 43 |
| Shear Strength, MPa | 200 to 520 | |
| 150 to 220 |
| Tensile Strength: Ultimate (UTS), MPa | 310 to 860 | |
| 220 to 420 |
| Tensile Strength: Yield (Proof), MPa | 170 to 760 | |
| 75 to 390 |
Thermal Properties
| Latent Heat of Fusion, J/g | 220 | |
| 210 |
| Maximum Temperature: Mechanical, °C | 220 | |
| 200 |
| Melting Completion (Liquidus), °C | 1060 | |
| 1080 |
| Melting Onset (Solidus), °C | 1020 | |
| 1070 |
| Specific Heat Capacity, J/kg-K | 390 | |
| 390 |
| Thermal Conductivity, W/m-K | 200 | |
| 350 |
| Thermal Expansion, µm/m-K | 18 | |
| 17 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 24 to 53 | |
| 92 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 24 to 54 | |
| 93 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 60 | |
| 31 |
| Density, g/cm3 | 8.9 | |
| 8.9 |
| Embodied Carbon, kg CO2/kg material | 4.7 | |
| 2.6 |
| Embodied Energy, MJ/kg | 73 | |
| 41 |
| Embodied Water, L/kg | 320 | |
| 310 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 30 to 120 | |
| 5.6 to 88 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 120 to 2390 | |
| 24 to 660 |
| Stiffness to Weight: Axial, points | 7.5 | |
| 7.2 |
| Stiffness to Weight: Bending, points | 18 | |
| 18 |
| Strength to Weight: Axial, points | 9.7 to 27 | |
| 6.9 to 13 |
| Strength to Weight: Bending, points | 11 to 23 | |
| 9.1 to 14 |
| Thermal Diffusivity, mm2/s | 59 | |
| 100 |
| Thermal Shock Resistance, points | 11 to 29 | |
| 7.8 to 15 |
Alloy Composition
| Aluminum (Al), % | 0 to 0.2 | |
| 0 |
| Antimony (Sb), % | 0 | |
| 0 to 0.0030 |
| Arsenic (As), % | 0 | |
| 0 to 0.012 |
| Beryllium (Be), % | 0.4 to 0.7 | |
| 0 |
| Bismuth (Bi), % | 0 | |
| 0 to 0.0030 |
| Cobalt (Co), % | 2.4 to 2.7 | |
| 0 |
| Copper (Cu), % | 95.6 to 97.2 | |
| 99.88 to 100 |
| Iron (Fe), % | 0 to 0.1 | |
| 0 |
| Lead (Pb), % | 0 | |
| 0 to 0.0040 |
| Nickel (Ni), % | 0 | |
| 0 to 0.050 |
| Silicon (Si), % | 0 to 0.2 | |
| 0 |
| Tellurium (Te), % | 0 | |
| 0 to 0.025 |
| Residuals, % | 0 | |
| 0 to 0.3 |