C23400 Brass vs. Grade 25 Titanium
C23400 brass belongs to the copper alloys classification, while grade 25 titanium belongs to the titanium alloys. There are 21 material properties with values for both materials. Properties with values for just one material (12, in this case) are not shown.
For each property being compared, the top bar is C23400 brass and the bottom bar is grade 25 titanium.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 110 | |
| 110 |
| Poisson's Ratio | 0.32 | |
| 0.32 |
| Shear Modulus, GPa | 42 | |
| 40 |
| Tensile Strength: Ultimate (UTS), MPa | 370 to 640 | |
| 1000 |
Thermal Properties
| Latent Heat of Fusion, J/g | 190 | |
| 410 |
| Maximum Temperature: Mechanical, °C | 160 | |
| 340 |
| Melting Completion (Liquidus), °C | 970 | |
| 1610 |
| Melting Onset (Solidus), °C | 930 | |
| 1560 |
| Specific Heat Capacity, J/kg-K | 390 | |
| 560 |
| Thermal Conductivity, W/m-K | 120 | |
| 7.1 |
| Thermal Expansion, µm/m-K | 19 | |
| 9.6 |
Otherwise Unclassified Properties
| Density, g/cm3 | 8.5 | |
| 4.5 |
| Embodied Carbon, kg CO2/kg material | 2.6 | |
| 43 |
| Embodied Energy, MJ/kg | 43 | |
| 700 |
| Embodied Water, L/kg | 320 | |
| 320 |
Common Calculations
| Stiffness to Weight: Axial, points | 7.2 | |
| 13 |
| Stiffness to Weight: Bending, points | 19 | |
| 35 |
| Strength to Weight: Axial, points | 12 to 21 | |
| 62 |
| Strength to Weight: Bending, points | 13 to 19 | |
| 50 |
| Thermal Diffusivity, mm2/s | 36 | |
| 2.8 |
| Thermal Shock Resistance, points | 12 to 22 | |
| 71 |
Alloy Composition
| Aluminum (Al), % | 0 | |
| 5.5 to 6.8 |
| Carbon (C), % | 0 | |
| 0 to 0.080 |
| Copper (Cu), % | 81 to 84 | |
| 0 |
| Hydrogen (H), % | 0 | |
| 0 to 0.013 |
| Iron (Fe), % | 0 to 0.050 | |
| 0 to 0.4 |
| Lead (Pb), % | 0 to 0.050 | |
| 0 |
| Nickel (Ni), % | 0 | |
| 0.3 to 0.8 |
| Nitrogen (N), % | 0 | |
| 0 to 0.050 |
| Oxygen (O), % | 0 | |
| 0 to 0.2 |
| Palladium (Pd), % | 0 | |
| 0.040 to 0.080 |
| Titanium (Ti), % | 0 | |
| 86.7 to 90.6 |
| Vanadium (V), % | 0 | |
| 3.5 to 4.5 |
| Zinc (Zn), % | 15.7 to 19 | |
| 0 |
| Residuals, % | 0 | |
| 0 to 0.4 |