C26200 Brass vs. C11400 Copper
Both C26200 brass and C11400 copper are copper alloys. They have 69% of their average alloy composition in common. There are 31 material properties with values for both materials. Properties with values for just one material (1, in this case) are not shown.
For each property being compared, the top bar is C26200 brass and the bottom bar is C11400 copper.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 110 | |
| 120 |
| Elongation at Break, % | 3.0 to 180 | |
| 2.8 to 51 |
| Poisson's Ratio | 0.31 | |
| 0.34 |
| Rockwell B Hardness | 55 to 93 | |
| 10 to 62 |
| Rockwell Superficial 30T Hardness | 26 to 78 | |
| 35 to 67 |
| Shear Modulus, GPa | 41 | |
| 43 |
| Shear Strength, MPa | 230 to 390 | |
| 150 to 210 |
| Tensile Strength: Ultimate (UTS), MPa | 330 to 770 | |
| 220 to 400 |
| Tensile Strength: Yield (Proof), MPa | 110 to 490 | |
| 75 to 400 |
Thermal Properties
| Latent Heat of Fusion, J/g | 180 | |
| 210 |
| Maximum Temperature: Mechanical, °C | 140 | |
| 200 |
| Melting Completion (Liquidus), °C | 950 | |
| 1080 |
| Melting Onset (Solidus), °C | 920 | |
| 1030 |
| Specific Heat Capacity, J/kg-K | 390 | |
| 390 |
| Thermal Conductivity, W/m-K | 120 | |
| 390 |
| Thermal Expansion, µm/m-K | 20 | |
| 17 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 28 | |
| 100 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 31 | |
| 100 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 25 | |
| 32 |
| Density, g/cm3 | 8.2 | |
| 9.0 |
| Embodied Carbon, kg CO2/kg material | 2.7 | |
| 2.6 |
| Embodied Energy, MJ/kg | 45 | |
| 42 |
| Embodied Water, L/kg | 320 | |
| 350 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 19 to 160 | |
| 11 to 90 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 62 to 1110 | |
| 24 to 680 |
| Stiffness to Weight: Axial, points | 7.2 | |
| 7.2 |
| Stiffness to Weight: Bending, points | 19 | |
| 18 |
| Strength to Weight: Axial, points | 11 to 26 | |
| 6.8 to 12 |
| Strength to Weight: Bending, points | 13 to 23 | |
| 9.1 to 14 |
| Thermal Diffusivity, mm2/s | 38 | |
| 110 |
| Thermal Shock Resistance, points | 11 to 26 | |
| 7.8 to 14 |
Alloy Composition
| Copper (Cu), % | 67 to 70 | |
| 99.84 to 99.966 |
| Iron (Fe), % | 0 to 0.050 | |
| 0 |
| Lead (Pb), % | 0 to 0.070 | |
| 0 |
| Silver (Ag), % | 0 | |
| 0.034 to 0.060 |
| Zinc (Zn), % | 29.6 to 33 | |
| 0 |
| Residuals, % | 0 | |
| 0 to 0.1 |