C38500 Bronze vs. S30452 Stainless Steel
C38500 bronze belongs to the copper alloys classification, while S30452 stainless steel belongs to the iron alloys. There are 29 material properties with values for both materials. Properties with values for just one material (5, in this case) are not shown.
For each property being compared, the top bar is C38500 bronze and the bottom bar is S30452 stainless steel.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 100 | |
| 200 |
| Elongation at Break, % | 17 | |
| 34 |
| Poisson's Ratio | 0.31 | |
| 0.28 |
| Shear Modulus, GPa | 37 | |
| 77 |
| Shear Strength, MPa | 230 | |
| 440 |
| Tensile Strength: Ultimate (UTS), MPa | 370 | |
| 660 |
| Tensile Strength: Yield (Proof), MPa | 130 | |
| 310 |
Thermal Properties
| Latent Heat of Fusion, J/g | 160 | |
| 290 |
| Maximum Temperature: Mechanical, °C | 110 | |
| 960 |
| Melting Completion (Liquidus), °C | 890 | |
| 1420 |
| Melting Onset (Solidus), °C | 880 | |
| 1380 |
| Specific Heat Capacity, J/kg-K | 380 | |
| 480 |
| Thermal Conductivity, W/m-K | 120 | |
| 16 |
| Thermal Expansion, µm/m-K | 21 | |
| 16 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 28 | |
| 2.4 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 31 | |
| 2.7 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 22 | |
| 15 |
| Density, g/cm3 | 8.1 | |
| 7.8 |
| Embodied Carbon, kg CO2/kg material | 2.6 | |
| 3.0 |
| Embodied Energy, MJ/kg | 45 | |
| 43 |
| Embodied Water, L/kg | 320 | |
| 150 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 48 | |
| 180 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 78 | |
| 250 |
| Stiffness to Weight: Axial, points | 7.0 | |
| 14 |
| Stiffness to Weight: Bending, points | 19 | |
| 25 |
| Strength to Weight: Axial, points | 13 | |
| 23 |
| Strength to Weight: Bending, points | 14 | |
| 22 |
| Thermal Diffusivity, mm2/s | 40 | |
| 4.2 |
| Thermal Shock Resistance, points | 12 | |
| 15 |
Alloy Composition
| Carbon (C), % | 0 | |
| 0 to 0.080 |
| Chromium (Cr), % | 0 | |
| 18 to 20 |
| Copper (Cu), % | 55 to 59 | |
| 0 |
| Iron (Fe), % | 0 to 0.35 | |
| 66.3 to 73.8 |
| Lead (Pb), % | 2.5 to 3.5 | |
| 0 |
| Manganese (Mn), % | 0 | |
| 0 to 2.0 |
| Nickel (Ni), % | 0 | |
| 8.0 to 10.5 |
| Nitrogen (N), % | 0 | |
| 0.16 to 0.3 |
| Phosphorus (P), % | 0 | |
| 0 to 0.045 |
| Silicon (Si), % | 0 | |
| 0 to 0.75 |
| Sulfur (S), % | 0 | |
| 0 to 0.030 |
| Zinc (Zn), % | 36.7 to 42.5 | |
| 0 |
| Residuals, % | 0 to 0.5 | |
| 0 |