C51000 Bronze vs. Solder Alloy 502
C51000 bronze belongs to the copper alloys classification, while solder alloy 502 belongs to the otherwise unclassified metals. There are 22 material properties with values for both materials. Properties with values for just one material (9, in this case) are not shown.
For each property being compared, the top bar is C51000 bronze and the bottom bar is solder alloy 502.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 110 | |
| 53 |
| Elongation at Break, % | 2.7 to 64 | |
| 34 |
| Poisson's Ratio | 0.34 | |
| 0.36 |
| Shear Modulus, GPa | 42 | |
| 19 |
| Tensile Strength: Ultimate (UTS), MPa | 330 to 780 | |
| 58 |
Thermal Properties
| Latent Heat of Fusion, J/g | 200 | |
| 66 |
| Melting Completion (Liquidus), °C | 1050 | |
| 350 |
| Melting Onset (Solidus), °C | 960 | |
| 220 |
| Specific Heat Capacity, J/kg-K | 380 | |
| 230 |
| Thermal Conductivity, W/m-K | 77 | |
| 47 |
| Thermal Expansion, µm/m-K | 18 | |
| 22 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 18 | |
| 12 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 18 | |
| 15 |
Otherwise Unclassified Properties
| Density, g/cm3 | 8.8 | |
| 7.4 |
| Embodied Carbon, kg CO2/kg material | 3.1 | |
| 15 |
| Embodied Energy, MJ/kg | 50 | |
| 260 |
Common Calculations
| Stiffness to Weight: Axial, points | 7.0 | |
| 4.0 |
| Stiffness to Weight: Bending, points | 18 | |
| 17 |
| Strength to Weight: Axial, points | 10 to 25 | |
| 2.2 |
| Strength to Weight: Bending, points | 12 to 21 | |
| 4.5 |
| Thermal Diffusivity, mm2/s | 23 | |
| 28 |
| Thermal Shock Resistance, points | 12 to 28 | |
| 3.6 |
Alloy Composition
| Aluminum (Al), % | 0 | |
| 0 to 0.0010 |
| Antimony (Sb), % | 0 | |
| 0 to 0.1 |
| Arsenic (As), % | 0 | |
| 0 to 0.030 |
| Bismuth (Bi), % | 0 | |
| 0 to 0.080 |
| Cadmium (Cd), % | 0 | |
| 0 to 0.0020 |
| Copper (Cu), % | 92.9 to 95.5 | |
| 3.5 to 4.5 |
| Gold (Au), % | 0 | |
| 0 to 0.050 |
| Indium (In), % | 0 | |
| 0 to 0.1 |
| Iron (Fe), % | 0 to 0.1 | |
| 0 to 0.020 |
| Lead (Pb), % | 0 to 0.050 | |
| 0 to 0.070 |
| Nickel (Ni), % | 0 | |
| 0 to 0.010 |
| Phosphorus (P), % | 0.030 to 0.35 | |
| 0 |
| Silver (Ag), % | 0 | |
| 0.8 to 1.2 |
| Tin (Sn), % | 4.5 to 5.8 | |
| 93.8 to 95.7 |
| Zinc (Zn), % | 0 to 0.3 | |
| 0 to 0.0010 |
| Residuals, % | 0 to 0.5 | |
| 0 |