C51100 Bronze vs. Commercially Pure Silver
C51100 bronze belongs to the copper alloys classification, while commercially pure silver belongs to the otherwise unclassified metals. There are 21 material properties with values for both materials. Properties with values for just one material (10, in this case) are not shown.
For each property being compared, the top bar is C51100 bronze and the bottom bar is commercially pure silver.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 110 | |
| 71 |
| Elongation at Break, % | 2.5 to 50 | |
| 1.1 to 29 |
| Poisson's Ratio | 0.34 | |
| 0.37 |
| Shear Modulus, GPa | 42 | |
| 26 |
| Shear Strength, MPa | 230 to 410 | |
| 120 to 190 |
| Tensile Strength: Ultimate (UTS), MPa | 330 to 720 | |
| 190 to 340 |
Thermal Properties
| Latent Heat of Fusion, J/g | 200 | |
| 110 |
| Melting Completion (Liquidus), °C | 1060 | |
| 960 |
| Melting Onset (Solidus), °C | 970 | |
| 960 |
| Specific Heat Capacity, J/kg-K | 380 | |
| 240 |
| Thermal Conductivity, W/m-K | 84 | |
| 420 |
| Thermal Expansion, µm/m-K | 18 | |
| 20 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 20 | |
| 100 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 20 | |
| 87 |
Otherwise Unclassified Properties
| Density, g/cm3 | 8.9 | |
| 10 |
Common Calculations
| Stiffness to Weight: Axial, points | 7.1 | |
| 3.8 |
| Stiffness to Weight: Bending, points | 18 | |
| 13 |
| Strength to Weight: Axial, points | 10 to 22 | |
| 4.9 to 8.9 |
| Strength to Weight: Bending, points | 12 to 20 | |
| 6.9 to 10 |
| Thermal Diffusivity, mm2/s | 25 | |
| 170 |
| Thermal Shock Resistance, points | 12 to 26 | |
| 9.5 to 17 |
Alloy Composition
| Copper (Cu), % | 93.8 to 96.5 | |
| 0 |
| Iron (Fe), % | 0 to 0.1 | |
| 0 |
| Lead (Pb), % | 0 to 0.050 | |
| 0 |
| Phosphorus (P), % | 0.030 to 0.35 | |
| 0 |
| Silver (Ag), % | 0 | |
| 99.9 to 100 |
| Tin (Sn), % | 3.5 to 4.9 | |
| 0 |
| Zinc (Zn), % | 0 to 0.3 | |
| 0 |
| Residuals, % | 0 | |
| 0 to 0.1 |