C54400 Bronze vs. C65400 Bronze
Both C54400 bronze and C65400 bronze are copper alloys. They have a moderately high 90% of their average alloy composition in common. There are 26 material properties with values for both materials. Properties with values for just one material (5, in this case) are not shown.
For each property being compared, the top bar is C54400 bronze and the bottom bar is C65400 bronze.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 110 | |
| 110 |
| Poisson's Ratio | 0.34 | |
| 0.34 |
| Rockwell B Hardness | 67 to 93 | |
| 82 to 120 |
| Rockwell Superficial 30T Hardness | 33 to 79 | |
| 71 to 92 |
| Shear Modulus, GPa | 40 | |
| 43 |
| Tensile Strength: Ultimate (UTS), MPa | 330 to 720 | |
| 500 to 1060 |
Thermal Properties
| Latent Heat of Fusion, J/g | 190 | |
| 260 |
| Maximum Temperature: Mechanical, °C | 170 | |
| 200 |
| Melting Completion (Liquidus), °C | 1000 | |
| 1020 |
| Melting Onset (Solidus), °C | 930 | |
| 960 |
| Specific Heat Capacity, J/kg-K | 370 | |
| 400 |
| Thermal Conductivity, W/m-K | 86 | |
| 36 |
| Thermal Expansion, µm/m-K | 18 | |
| 17 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 19 | |
| 7.0 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 19 | |
| 7.3 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 31 | |
| 31 |
| Density, g/cm3 | 8.9 | |
| 8.7 |
| Embodied Carbon, kg CO2/kg material | 2.9 | |
| 2.8 |
| Embodied Energy, MJ/kg | 48 | |
| 45 |
| Embodied Water, L/kg | 340 | |
| 310 |
Common Calculations
| Stiffness to Weight: Axial, points | 6.8 | |
| 7.3 |
| Stiffness to Weight: Bending, points | 18 | |
| 19 |
| Strength to Weight: Axial, points | 10 to 22 | |
| 16 to 34 |
| Strength to Weight: Bending, points | 12 to 20 | |
| 16 to 27 |
| Thermal Diffusivity, mm2/s | 26 | |
| 10 |
| Thermal Shock Resistance, points | 12 to 26 | |
| 18 to 39 |
Alloy Composition
| Chromium (Cr), % | 0 | |
| 0.010 to 0.12 |
| Copper (Cu), % | 85.4 to 91.5 | |
| 93.8 to 96.1 |
| Iron (Fe), % | 0 to 0.1 | |
| 0 |
| Lead (Pb), % | 3.5 to 4.5 | |
| 0 to 0.050 |
| Phosphorus (P), % | 0.010 to 0.5 | |
| 0 |
| Silicon (Si), % | 0 | |
| 2.7 to 3.4 |
| Tin (Sn), % | 3.5 to 4.5 | |
| 1.2 to 1.9 |
| Zinc (Zn), % | 1.5 to 4.5 | |
| 0 to 0.5 |
| Residuals, % | 0 | |
| 0 to 0.2 |