C61000 Bronze vs. Grade 5 Titanium
C61000 bronze belongs to the copper alloys classification, while grade 5 titanium belongs to the titanium alloys. There are 29 material properties with values for both materials. Properties with values for just one material (4, in this case) are not shown.
For each property being compared, the top bar is C61000 bronze and the bottom bar is grade 5 titanium.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 110 | |
| 110 |
| Elongation at Break, % | 29 to 50 | |
| 8.6 to 11 |
| Poisson's Ratio | 0.34 | |
| 0.32 |
| Shear Modulus, GPa | 42 | |
| 40 |
| Shear Strength, MPa | 280 to 300 | |
| 600 to 710 |
| Tensile Strength: Ultimate (UTS), MPa | 390 to 460 | |
| 1000 to 1190 |
| Tensile Strength: Yield (Proof), MPa | 150 to 190 | |
| 910 to 1110 |
Thermal Properties
| Latent Heat of Fusion, J/g | 220 | |
| 410 |
| Maximum Temperature: Mechanical, °C | 210 | |
| 330 |
| Melting Completion (Liquidus), °C | 1040 | |
| 1610 |
| Melting Onset (Solidus), °C | 990 | |
| 1650 |
| Specific Heat Capacity, J/kg-K | 420 | |
| 560 |
| Thermal Conductivity, W/m-K | 69 | |
| 6.8 |
| Thermal Expansion, µm/m-K | 18 | |
| 8.9 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 15 | |
| 1.0 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 16 | |
| 2.0 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 29 | |
| 36 |
| Density, g/cm3 | 8.5 | |
| 4.4 |
| Embodied Carbon, kg CO2/kg material | 3.0 | |
| 38 |
| Embodied Energy, MJ/kg | 49 | |
| 610 |
| Embodied Water, L/kg | 370 | |
| 200 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 110 to 160 | |
| 100 to 110 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 100 to 160 | |
| 3980 to 5880 |
| Stiffness to Weight: Axial, points | 7.4 | |
| 13 |
| Stiffness to Weight: Bending, points | 19 | |
| 35 |
| Strength to Weight: Axial, points | 13 to 15 | |
| 62 to 75 |
| Strength to Weight: Bending, points | 14 to 16 | |
| 50 to 56 |
| Thermal Diffusivity, mm2/s | 19 | |
| 2.7 |
| Thermal Shock Resistance, points | 14 to 16 | |
| 76 to 91 |
Alloy Composition
| Aluminum (Al), % | 6.0 to 8.5 | |
| 5.5 to 6.8 |
| Carbon (C), % | 0 | |
| 0 to 0.080 |
| Copper (Cu), % | 90.2 to 94 | |
| 0 |
| Hydrogen (H), % | 0 | |
| 0 to 0.015 |
| Iron (Fe), % | 0 to 0.5 | |
| 0 to 0.4 |
| Lead (Pb), % | 0 to 0.020 | |
| 0 |
| Nitrogen (N), % | 0 | |
| 0 to 0.050 |
| Oxygen (O), % | 0 | |
| 0 to 0.2 |
| Silicon (Si), % | 0 to 0.1 | |
| 0 |
| Titanium (Ti), % | 0 | |
| 87.4 to 91 |
| Vanadium (V), % | 0 | |
| 3.5 to 4.5 |
| Yttrium (Y), % | 0 | |
| 0 to 0.0050 |
| Zinc (Zn), % | 0 to 0.2 | |
| 0 |
| Residuals, % | 0 | |
| 0 to 0.4 |