C61300 Bronze vs. ASTM A356 Grade 10
C61300 bronze belongs to the copper alloys classification, while ASTM A356 grade 10 belongs to the iron alloys. There are 28 material properties with values for both materials. Properties with values for just one material (5, in this case) are not shown.
For each property being compared, the top bar is C61300 bronze and the bottom bar is ASTM A356 grade 10.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 110 | |
| 190 |
| Elongation at Break, % | 34 to 40 | |
| 23 |
| Poisson's Ratio | 0.34 | |
| 0.29 |
| Shear Modulus, GPa | 43 | |
| 74 |
| Tensile Strength: Ultimate (UTS), MPa | 550 to 580 | |
| 670 |
| Tensile Strength: Yield (Proof), MPa | 230 to 310 | |
| 430 |
Thermal Properties
| Latent Heat of Fusion, J/g | 220 | |
| 260 |
| Maximum Temperature: Mechanical, °C | 210 | |
| 460 |
| Melting Completion (Liquidus), °C | 1050 | |
| 1470 |
| Melting Onset (Solidus), °C | 1040 | |
| 1430 |
| Specific Heat Capacity, J/kg-K | 420 | |
| 470 |
| Thermal Conductivity, W/m-K | 55 | |
| 39 |
| Thermal Expansion, µm/m-K | 18 | |
| 13 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 12 | |
| 7.6 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 13 | |
| 8.8 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 29 | |
| 3.9 |
| Density, g/cm3 | 8.5 | |
| 7.9 |
| Embodied Carbon, kg CO2/kg material | 3.0 | |
| 1.8 |
| Embodied Energy, MJ/kg | 49 | |
| 23 |
| Embodied Water, L/kg | 370 | |
| 59 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 150 to 190 | |
| 130 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 230 to 410 | |
| 480 |
| Stiffness to Weight: Axial, points | 7.5 | |
| 13 |
| Stiffness to Weight: Bending, points | 19 | |
| 24 |
| Strength to Weight: Axial, points | 18 to 19 | |
| 24 |
| Strength to Weight: Bending, points | 18 | |
| 22 |
| Thermal Diffusivity, mm2/s | 15 | |
| 11 |
| Thermal Shock Resistance, points | 19 to 20 | |
| 19 |
Alloy Composition
| Aluminum (Al), % | 6.0 to 7.5 | |
| 0 |
| Carbon (C), % | 0 | |
| 0 to 0.2 |
| Chromium (Cr), % | 0 | |
| 2.0 to 2.8 |
| Copper (Cu), % | 88 to 91.8 | |
| 0 |
| Iron (Fe), % | 2.0 to 3.0 | |
| 94.4 to 96.6 |
| Lead (Pb), % | 0 to 0.010 | |
| 0 |
| Manganese (Mn), % | 0 to 0.2 | |
| 0.5 to 0.8 |
| Molybdenum (Mo), % | 0 | |
| 0.9 to 1.2 |
| Nickel (Ni), % | 0 to 0.15 | |
| 0 |
| Phosphorus (P), % | 0 to 0.015 | |
| 0 to 0.035 |
| Silicon (Si), % | 0 to 0.1 | |
| 0 to 0.6 |
| Sulfur (S), % | 0 | |
| 0 to 0.030 |
| Tin (Sn), % | 0.2 to 0.5 | |
| 0 |
| Zinc (Zn), % | 0 to 0.2 | |
| 0 |
| Residuals, % | 0 to 0.2 | |
| 0 |