C61400 Bronze vs. C78200 Nickel Silver
Both C61400 bronze and C78200 nickel silver are copper alloys. They have 66% of their average alloy composition in common. There are 29 material properties with values for both materials. Properties with values for just one material (2, in this case) are not shown.
For each property being compared, the top bar is C61400 bronze and the bottom bar is C78200 nickel silver.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 110 | |
| 110 |
| Elongation at Break, % | 34 to 40 | |
| 3.0 to 40 |
| Poisson's Ratio | 0.34 | |
| 0.32 |
| Shear Modulus, GPa | 43 | |
| 43 |
| Shear Strength, MPa | 370 to 380 | |
| 280 to 400 |
| Tensile Strength: Ultimate (UTS), MPa | 540 to 570 | |
| 370 to 630 |
| Tensile Strength: Yield (Proof), MPa | 220 to 270 | |
| 170 to 570 |
Thermal Properties
| Latent Heat of Fusion, J/g | 220 | |
| 190 |
| Maximum Temperature: Mechanical, °C | 220 | |
| 160 |
| Melting Completion (Liquidus), °C | 1050 | |
| 1000 |
| Melting Onset (Solidus), °C | 1040 | |
| 970 |
| Specific Heat Capacity, J/kg-K | 420 | |
| 390 |
| Thermal Conductivity, W/m-K | 67 | |
| 48 |
| Thermal Expansion, µm/m-K | 18 | |
| 19 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 14 | |
| 11 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 15 | |
| 12 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 28 | |
| 28 |
| Density, g/cm3 | 8.5 | |
| 8.4 |
| Embodied Carbon, kg CO2/kg material | 3.0 | |
| 3.3 |
| Embodied Energy, MJ/kg | 48 | |
| 52 |
| Embodied Water, L/kg | 360 | |
| 310 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 160 to 170 | |
| 18 to 120 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 210 to 310 | |
| 130 to 1440 |
| Stiffness to Weight: Axial, points | 7.5 | |
| 7.4 |
| Stiffness to Weight: Bending, points | 19 | |
| 19 |
| Strength to Weight: Axial, points | 18 to 19 | |
| 12 to 21 |
| Strength to Weight: Bending, points | 17 to 18 | |
| 14 to 19 |
| Thermal Diffusivity, mm2/s | 19 | |
| 15 |
| Thermal Shock Resistance, points | 18 to 20 | |
| 12 to 21 |
Alloy Composition
| Aluminum (Al), % | 6.0 to 8.0 | |
| 0 |
| Copper (Cu), % | 86 to 92.5 | |
| 63 to 67 |
| Iron (Fe), % | 1.5 to 3.5 | |
| 0 to 0.35 |
| Lead (Pb), % | 0 to 0.010 | |
| 1.5 to 2.5 |
| Manganese (Mn), % | 0 to 1.0 | |
| 0 to 0.5 |
| Nickel (Ni), % | 0 | |
| 7.0 to 9.0 |
| Phosphorus (P), % | 0 to 0.015 | |
| 0 |
| Zinc (Zn), % | 0 to 1.0 | |
| 20.2 to 28.5 |
| Residuals, % | 0 | |
| 0 to 0.5 |