C67400 Bronze vs. C94100 Bronze
Both C67400 bronze and C94100 bronze are copper alloys. They have 60% of their average alloy composition in common. There are 26 material properties with values for both materials. Properties with values for just one material (4, in this case) are not shown.
For each property being compared, the top bar is C67400 bronze and the bottom bar is C94100 bronze.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 110 | |
| 92 |
| Elongation at Break, % | 22 to 28 | |
| 7.8 |
| Poisson's Ratio | 0.31 | |
| 0.36 |
| Shear Modulus, GPa | 41 | |
| 34 |
| Tensile Strength: Ultimate (UTS), MPa | 480 to 610 | |
| 190 |
| Tensile Strength: Yield (Proof), MPa | 250 to 370 | |
| 130 |
Thermal Properties
| Latent Heat of Fusion, J/g | 190 | |
| 160 |
| Maximum Temperature: Mechanical, °C | 130 | |
| 130 |
| Melting Completion (Liquidus), °C | 890 | |
| 870 |
| Melting Onset (Solidus), °C | 870 | |
| 790 |
| Specific Heat Capacity, J/kg-K | 400 | |
| 330 |
| Thermal Expansion, µm/m-K | 21 | |
| 20 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 23 | |
| 9.0 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 26 | |
| 8.8 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 23 | |
| 29 |
| Density, g/cm3 | 7.9 | |
| 9.2 |
| Embodied Carbon, kg CO2/kg material | 2.8 | |
| 3.0 |
| Embodied Energy, MJ/kg | 48 | |
| 48 |
| Embodied Water, L/kg | 330 | |
| 370 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 110 to 120 | |
| 14 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 300 to 660 | |
| 97 |
| Stiffness to Weight: Axial, points | 7.5 | |
| 5.5 |
| Stiffness to Weight: Bending, points | 20 | |
| 16 |
| Strength to Weight: Axial, points | 17 to 22 | |
| 5.8 |
| Strength to Weight: Bending, points | 17 to 20 | |
| 8.1 |
| Thermal Shock Resistance, points | 16 to 20 | |
| 7.6 |
Alloy Composition
| Aluminum (Al), % | 0.5 to 2.0 | |
| 0 to 0.0050 |
| Antimony (Sb), % | 0 | |
| 0 to 0.8 |
| Copper (Cu), % | 57 to 60 | |
| 72 to 79 |
| Iron (Fe), % | 0 to 0.35 | |
| 0 to 0.25 |
| Lead (Pb), % | 0 to 0.5 | |
| 18 to 22 |
| Manganese (Mn), % | 2.0 to 3.5 | |
| 0 |
| Nickel (Ni), % | 0 to 0.25 | |
| 0 to 1.0 |
| Phosphorus (P), % | 0 | |
| 0 to 1.5 |
| Silicon (Si), % | 0.5 to 1.5 | |
| 0 to 0.0050 |
| Sulfur (S), % | 0 | |
| 0 to 0.080 |
| Tin (Sn), % | 0 to 0.3 | |
| 4.5 to 6.5 |
| Zinc (Zn), % | 31.1 to 40 | |
| 0 to 1.0 |
| Residuals, % | 0 | |
| 0 to 1.3 |