C68700 Brass vs. Solder Alloy 101
C68700 brass belongs to the copper alloys classification, while solder alloy 101 belongs to the otherwise unclassified metals. There are 24 material properties with values for both materials. Properties with values for just one material (5, in this case) are not shown.
For each property being compared, the top bar is C68700 brass and the bottom bar is solder alloy 101.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 110 | |
| 38 |
| Poisson's Ratio | 0.32 | |
| 0.39 |
| Shear Modulus, GPa | 41 | |
| 14 |
| Tensile Strength: Ultimate (UTS), MPa | 390 | |
| 31 |
| Tensile Strength: Yield (Proof), MPa | 140 | |
| 27 |
Thermal Properties
| Latent Heat of Fusion, J/g | 190 | |
| 46 |
| Melting Completion (Liquidus), °C | 970 | |
| 180 |
| Melting Onset (Solidus), °C | 930 | |
| 180 |
| Specific Heat Capacity, J/kg-K | 400 | |
| 190 |
| Thermal Conductivity, W/m-K | 100 | |
| 51 |
| Thermal Expansion, µm/m-K | 19 | |
| 25 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 23 | |
| 12 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 25 | |
| 12 |
Otherwise Unclassified Properties
| Density, g/cm3 | 8.3 | |
| 8.8 |
| Embodied Carbon, kg CO2/kg material | 2.8 | |
| 11 |
| Embodied Energy, MJ/kg | 46 | |
| 180 |
| Embodied Water, L/kg | 340 | |
| 930 |
Common Calculations
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 90 | |
| 9.9 |
| Stiffness to Weight: Axial, points | 7.3 | |
| 2.4 |
| Stiffness to Weight: Bending, points | 19 | |
| 13 |
| Strength to Weight: Axial, points | 13 | |
| 1.0 |
| Strength to Weight: Bending, points | 14 | |
| 2.5 |
| Thermal Diffusivity, mm2/s | 30 | |
| 31 |
| Thermal Shock Resistance, points | 13 | |
| 2.4 |
Alloy Composition
| Aluminum (Al), % | 1.8 to 2.5 | |
| 0 to 0.0010 |
| Antimony (Sb), % | 0 | |
| 0 to 0.2 |
| Arsenic (As), % | 0.020 to 0.1 | |
| 0 to 0.030 |
| Bismuth (Bi), % | 0 | |
| 0 to 0.1 |
| Cadmium (Cd), % | 0 | |
| 0 to 0.0020 |
| Copper (Cu), % | 76 to 79 | |
| 0 to 0.080 |
| Gold (Au), % | 0 | |
| 0 to 0.050 |
| Indium (In), % | 0 | |
| 0 to 0.1 |
| Iron (Fe), % | 0 to 0.060 | |
| 0 to 0.020 |
| Lead (Pb), % | 0 to 0.070 | |
| 35.8 to 37.5 |
| Nickel (Ni), % | 0 | |
| 0 to 0.010 |
| Silver (Ag), % | 0 | |
| 0 to 0.1 |
| Tin (Sn), % | 0 | |
| 62.5 to 63.5 |
| Zinc (Zn), % | 17.8 to 22.2 | |
| 0 to 0.0010 |
| Residuals, % | 0 to 0.5 | |
| 0 |