C77300 Nickel Silver vs. Grade 23 Titanium
C77300 nickel silver belongs to the copper alloys classification, while grade 23 titanium belongs to the titanium alloys. There are 22 material properties with values for both materials. Properties with values for just one material (11, in this case) are not shown.
For each property being compared, the top bar is C77300 nickel silver and the bottom bar is grade 23 titanium.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 110 | |
| 110 |
| Poisson's Ratio | 0.3 | |
| 0.32 |
| Shear Modulus, GPa | 42 | |
| 40 |
| Tensile Strength: Ultimate (UTS), MPa | 540 | |
| 930 to 940 |
Thermal Properties
| Latent Heat of Fusion, J/g | 180 | |
| 410 |
| Maximum Temperature: Mechanical, °C | 130 | |
| 340 |
| Melting Completion (Liquidus), °C | 940 | |
| 1610 |
| Melting Onset (Solidus), °C | 920 | |
| 1560 |
| Specific Heat Capacity, J/kg-K | 390 | |
| 560 |
| Thermal Expansion, µm/m-K | 20 | |
| 9.4 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 5.5 | |
| 1.0 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 6.3 | |
| 2.0 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 26 | |
| 36 |
| Density, g/cm3 | 7.9 | |
| 4.4 |
| Embodied Carbon, kg CO2/kg material | 3.5 | |
| 38 |
| Embodied Energy, MJ/kg | 56 | |
| 610 |
| Embodied Water, L/kg | 310 | |
| 200 |
Common Calculations
| Stiffness to Weight: Axial, points | 7.7 | |
| 13 |
| Stiffness to Weight: Bending, points | 20 | |
| 35 |
| Strength to Weight: Axial, points | 19 | |
| 58 to 59 |
| Strength to Weight: Bending, points | 19 | |
| 48 |
| Thermal Shock Resistance, points | 17 | |
| 67 to 68 |
Alloy Composition
| Aluminum (Al), % | 0 to 0.010 | |
| 5.5 to 6.5 |
| Carbon (C), % | 0 | |
| 0 to 0.080 |
| Copper (Cu), % | 46 to 50 | |
| 0 |
| Hydrogen (H), % | 0 | |
| 0 to 0.013 |
| Iron (Fe), % | 0 | |
| 0 to 0.25 |
| Lead (Pb), % | 0 to 0.050 | |
| 0 |
| Nickel (Ni), % | 9.0 to 11 | |
| 0 |
| Nitrogen (N), % | 0 | |
| 0 to 0.030 |
| Oxygen (O), % | 0 | |
| 0 to 0.13 |
| Phosphorus (P), % | 0 to 0.25 | |
| 0 |
| Silicon (Si), % | 0.040 to 0.25 | |
| 0 |
| Titanium (Ti), % | 0 | |
| 88.1 to 91 |
| Vanadium (V), % | 0 | |
| 3.5 to 4.5 |
| Zinc (Zn), % | 37.9 to 45 | |
| 0 |
| Residuals, % | 0 | |
| 0 to 0.4 |