C77600 Nickel Silver vs. Grade 23 Titanium
C77600 nickel silver belongs to the copper alloys classification, while grade 23 titanium belongs to the titanium alloys. There are 27 material properties with values for both materials. Properties with values for just one material (6, in this case) are not shown.
For each property being compared, the top bar is C77600 nickel silver and the bottom bar is grade 23 titanium.
Metric UnitsUS Customary Units
Mechanical Properties
Elastic (Young's, Tensile) Modulus, GPa | 110 | |
110 |
Elongation at Break, % | 30 | |
6.7 to 11 |
Poisson's Ratio | 0.3 | |
0.32 |
Shear Modulus, GPa | 43 | |
40 |
Shear Strength, MPa | 410 | |
540 to 570 |
Tensile Strength: Ultimate (UTS), MPa | 630 | |
930 to 940 |
Tensile Strength: Yield (Proof), MPa | 320 | |
850 to 870 |
Thermal Properties
Latent Heat of Fusion, J/g | 180 | |
410 |
Maximum Temperature: Mechanical, °C | 140 | |
340 |
Melting Completion (Liquidus), °C | 830 | |
1610 |
Melting Onset (Solidus), °C | 790 | |
1560 |
Specific Heat Capacity, J/kg-K | 390 | |
560 |
Thermal Expansion, µm/m-K | 20 | |
9.4 |
Electrical Properties
Electrical Conductivity: Equal Volume, % IACS | 27 | |
1.0 |
Electrical Conductivity: Equal Weight (Specific), % IACS | 31 | |
2.0 |
Otherwise Unclassified Properties
Base Metal Price, % relative | 27 | |
36 |
Density, g/cm3 | 7.9 | |
4.4 |
Embodied Carbon, kg CO2/kg material | 3.7 | |
38 |
Embodied Energy, MJ/kg | 60 | |
610 |
Embodied Water, L/kg | 310 | |
200 |
Common Calculations
Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 160 | |
61 to 100 |
Resilience: Unit (Modulus of Resilience), kJ/m3 | 470 | |
3430 to 3560 |
Stiffness to Weight: Axial, points | 7.9 | |
13 |
Stiffness to Weight: Bending, points | 20 | |
35 |
Strength to Weight: Axial, points | 22 | |
58 to 59 |
Strength to Weight: Bending, points | 21 | |
48 |
Thermal Shock Resistance, points | 20 | |
67 to 68 |
Alloy Composition
Aluminum (Al), % | 0 | |
5.5 to 6.5 |
Carbon (C), % | 0 | |
0 to 0.080 |
Copper (Cu), % | 42 to 45 | |
0 |
Hydrogen (H), % | 0 | |
0 to 0.013 |
Iron (Fe), % | 0 to 0.2 | |
0 to 0.25 |
Lead (Pb), % | 0 to 0.25 | |
0 |
Manganese (Mn), % | 0 to 0.25 | |
0 |
Nickel (Ni), % | 12 to 14 | |
0 |
Nitrogen (N), % | 0 | |
0 to 0.030 |
Oxygen (O), % | 0 | |
0 to 0.13 |
Tin (Sn), % | 0 to 0.15 | |
0 |
Titanium (Ti), % | 0 | |
88.1 to 91 |
Vanadium (V), % | 0 | |
3.5 to 4.5 |
Zinc (Zn), % | 39.7 to 46 | |
0 |
Residuals, % | 0 | |
0 to 0.4 |