C95410 Bronze vs. AWS E383

C95410 bronze belongs to the copper alloys classification, while AWS E383 belongs to the iron alloys. There are 22 material properties with values for both materials. Properties with values for just one material (8, in this case) are not shown.

For each property being compared, the top bar is C95410 bronze and the bottom bar is AWS E383.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 120
210
Elongation at Break, % 9.1 to 13
34
Poisson's Ratio 0.34
0.28
Shear Modulus, GPa 43
80
Tensile Strength: Ultimate (UTS), MPa 620 to 740
580

Thermal Properties

Latent Heat of Fusion, J/g 230
320
Melting Completion (Liquidus), °C 1040
1420
Melting Onset (Solidus), °C 1030
1370
Specific Heat Capacity, J/kg-K 440
470
Thermal Conductivity, W/m-K 59
12
Thermal Expansion, µm/m-K 18
14

Otherwise Unclassified Properties

Base Metal Price, % relative 28
37
Density, g/cm3 8.2
8.1
Embodied Carbon, kg CO2/kg material 3.3
6.4
Embodied Energy, MJ/kg 54
89
Embodied Water, L/kg 390
240

Common Calculations

Stiffness to Weight: Axial, points 7.8
14
Stiffness to Weight: Bending, points 20
24
Strength to Weight: Axial, points 21 to 25
20
Strength to Weight: Bending, points 20 to 22
19
Thermal Diffusivity, mm2/s 16
3.1
Thermal Shock Resistance, points 22 to 26
15

Alloy Composition

Aluminum (Al), % 10 to 11.5
0
Carbon (C), % 0
0 to 0.030
Chromium (Cr), % 0
26.5 to 29
Copper (Cu), % 83 to 85.5
0.6 to 1.5
Iron (Fe), % 3.0 to 5.0
28.8 to 39.2
Manganese (Mn), % 0 to 0.5
0.5 to 2.5
Molybdenum (Mo), % 0
3.2 to 4.2
Nickel (Ni), % 1.5 to 2.5
30 to 33
Phosphorus (P), % 0
0 to 0.020
Silicon (Si), % 0
0 to 0.9
Sulfur (S), % 0
0 to 0.020
Residuals, % 0 to 0.5
0