C95600 Bronze vs. EN 1.8828 Steel

C95600 bronze belongs to the copper alloys classification, while EN 1.8828 steel belongs to the iron alloys. There are 28 material properties with values for both materials. Properties with values for just one material (4, in this case) are not shown.

For each property being compared, the top bar is C95600 bronze and the bottom bar is EN 1.8828 steel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 110
190
Elongation at Break, % 15
22
Poisson's Ratio 0.34
0.29
Shear Modulus, GPa 42
73
Tensile Strength: Ultimate (UTS), MPa 500
580
Tensile Strength: Yield (Proof), MPa 230
440

Thermal Properties

Latent Heat of Fusion, J/g 260
250
Maximum Temperature: Mechanical, °C 210
400
Melting Completion (Liquidus), °C 1000
1460
Melting Onset (Solidus), °C 980
1420
Specific Heat Capacity, J/kg-K 430
470
Thermal Conductivity, W/m-K 39
49
Thermal Expansion, µm/m-K 17
13

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 8.0
7.3
Electrical Conductivity: Equal Weight (Specific), % IACS 8.7
8.4

Otherwise Unclassified Properties

Base Metal Price, % relative 28
2.3
Density, g/cm3 8.3
7.8
Embodied Carbon, kg CO2/kg material 3.0
1.6
Embodied Energy, MJ/kg 50
21
Embodied Water, L/kg 360
48

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 60
120
Resilience: Unit (Modulus of Resilience), kJ/m3 230
530
Stiffness to Weight: Axial, points 7.5
13
Stiffness to Weight: Bending, points 19
24
Strength to Weight: Axial, points 17
21
Strength to Weight: Bending, points 17
20
Thermal Diffusivity, mm2/s 11
13
Thermal Shock Resistance, points 18
17

Alloy Composition

Aluminum (Al), % 6.0 to 8.0
0.020 to 0.040
Carbon (C), % 0
0 to 0.16
Copper (Cu), % 88 to 92.2
0
Iron (Fe), % 0
96.7 to 99.98
Manganese (Mn), % 0
0 to 1.7
Molybdenum (Mo), % 0
0 to 0.2
Nickel (Ni), % 0 to 0.25
0 to 0.5
Niobium (Nb), % 0
0 to 0.050
Nitrogen (N), % 0
0 to 0.020
Phosphorus (P), % 0
0 to 0.020
Silicon (Si), % 1.8 to 3.2
0 to 0.5
Sulfur (S), % 0
0 to 0.0050
Titanium (Ti), % 0
0 to 0.050
Vanadium (V), % 0
0 to 0.1
Residuals, % 0 to 1.0
0