C99400 Brass vs. EN 2.4878 Nickel
C99400 brass belongs to the copper alloys classification, while EN 2.4878 nickel belongs to the nickel alloys. There are 22 material properties with values for both materials. Properties with values for just one material (8, in this case) are not shown.
For each property being compared, the top bar is C99400 brass and the bottom bar is EN 2.4878 nickel.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 120 | |
| 200 |
| Poisson's Ratio | 0.34 | |
| 0.29 |
| Shear Modulus, GPa | 44 | |
| 78 |
| Tensile Strength: Ultimate (UTS), MPa | 460 to 550 | |
| 1210 to 1250 |
| Tensile Strength: Yield (Proof), MPa | 230 to 370 | |
| 740 to 780 |
Thermal Properties
| Latent Heat of Fusion, J/g | 230 | |
| 330 |
| Maximum Temperature: Mechanical, °C | 200 | |
| 1030 |
| Melting Completion (Liquidus), °C | 1070 | |
| 1370 |
| Melting Onset (Solidus), °C | 1020 | |
| 1320 |
| Specific Heat Capacity, J/kg-K | 400 | |
| 460 |
| Thermal Expansion, µm/m-K | 17 | |
| 12 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 30 | |
| 80 |
| Density, g/cm3 | 8.7 | |
| 8.3 |
| Embodied Carbon, kg CO2/kg material | 2.8 | |
| 10 |
| Embodied Energy, MJ/kg | 45 | |
| 150 |
| Embodied Water, L/kg | 310 | |
| 370 |
Common Calculations
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 230 to 590 | |
| 1370 to 1540 |
| Stiffness to Weight: Axial, points | 7.5 | |
| 13 |
| Stiffness to Weight: Bending, points | 19 | |
| 24 |
| Strength to Weight: Axial, points | 15 to 17 | |
| 41 to 42 |
| Strength to Weight: Bending, points | 15 to 17 | |
| 31 |
| Thermal Shock Resistance, points | 16 to 19 | |
| 37 to 39 |
Alloy Composition
| Aluminum (Al), % | 0.5 to 2.0 | |
| 1.2 to 1.6 |
| Boron (B), % | 0 | |
| 0.010 to 0.015 |
| Carbon (C), % | 0 | |
| 0.030 to 0.070 |
| Chromium (Cr), % | 0 | |
| 23 to 25 |
| Cobalt (Co), % | 0 | |
| 19 to 21 |
| Copper (Cu), % | 83.5 to 96.5 | |
| 0 to 0.2 |
| Iron (Fe), % | 1.0 to 3.0 | |
| 0 to 1.0 |
| Lead (Pb), % | 0 to 0.25 | |
| 0 |
| Manganese (Mn), % | 0 to 0.5 | |
| 0 to 0.5 |
| Molybdenum (Mo), % | 0 | |
| 1.0 to 2.0 |
| Nickel (Ni), % | 1.0 to 3.5 | |
| 43.6 to 52.2 |
| Niobium (Nb), % | 0 | |
| 0.7 to 1.2 |
| Phosphorus (P), % | 0 | |
| 0 to 0.010 |
| Silicon (Si), % | 0.5 to 2.0 | |
| 0 to 0.5 |
| Sulfur (S), % | 0 | |
| 0 to 0.0070 |
| Tantalum (Ta), % | 0 | |
| 0 to 0.050 |
| Titanium (Ti), % | 0 | |
| 2.8 to 3.2 |
| Zinc (Zn), % | 0.5 to 5.0 | |
| 0 |
| Zirconium (Zr), % | 0 | |
| 0.030 to 0.070 |
| Residuals, % | 0 to 0.3 | |
| 0 |