K93600 Alloy vs. R30605 Cobalt
K93600 alloy belongs to the iron alloys classification, while R30605 cobalt belongs to the cobalt alloys. There are 17 material properties with values for both materials. Properties with values for just one material (13, in this case) are not shown.
For each property being compared, the top bar is K93600 alloy and the bottom bar is R30605 cobalt.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 140 | |
| 210 |
| Elongation at Break, % | 5.0 to 35 | |
| 34 |
| Tensile Strength: Ultimate (UTS), MPa | 480 to 810 | |
| 1130 to 1900 |
| Tensile Strength: Yield (Proof), MPa | 280 to 750 | |
| 470 to 1600 |
Thermal Properties
| Melting Onset (Solidus), °C | 1430 | |
| 1330 |
| Specific Heat Capacity, J/kg-K | 520 | |
| 410 |
| Thermal Conductivity, W/m-K | 13 | |
| 9.6 |
| Thermal Expansion, µm/m-K | 7.3 | |
| 12 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 2.2 | |
| 2.0 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 2.4 | |
| 1.8 |
Otherwise Unclassified Properties
| Density, g/cm3 | 8.1 | |
| 9.6 |
Common Calculations
| Stiffness to Weight: Axial, points | 9.4 | |
| 12 |
| Stiffness to Weight: Bending, points | 21 | |
| 21 |
| Strength to Weight: Axial, points | 16 to 28 | |
| 33 to 55 |
| Strength to Weight: Bending, points | 17 to 24 | |
| 25 to 36 |
| Thermal Diffusivity, mm2/s | 3.1 | |
| 2.5 |
| Thermal Shock Resistance, points | 34 to 57 | |
| 31 to 52 |