N06007 Nickel vs. EN 1.4935 Stainless Steel
N06007 nickel belongs to the nickel alloys classification, while EN 1.4935 stainless steel belongs to the iron alloys. They have a modest 34% of their average alloy composition in common, which, by itself, doesn't mean much. There are 28 material properties with values for both materials. Properties with values for just one material (4, in this case) are not shown.
For each property being compared, the top bar is N06007 nickel and the bottom bar is EN 1.4935 stainless steel.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 200 | |
| 200 |
| Elongation at Break, % | 38 | |
| 16 to 18 |
| Fatigue Strength, MPa | 330 | |
| 350 to 400 |
| Poisson's Ratio | 0.29 | |
| 0.28 |
| Shear Modulus, GPa | 79 | |
| 76 |
| Shear Strength, MPa | 470 | |
| 480 to 540 |
| Tensile Strength: Ultimate (UTS), MPa | 690 | |
| 780 to 880 |
| Tensile Strength: Yield (Proof), MPa | 260 | |
| 570 to 670 |
Thermal Properties
| Latent Heat of Fusion, J/g | 320 | |
| 270 |
| Maximum Temperature: Mechanical, °C | 990 | |
| 740 |
| Melting Completion (Liquidus), °C | 1340 | |
| 1460 |
| Melting Onset (Solidus), °C | 1260 | |
| 1420 |
| Specific Heat Capacity, J/kg-K | 450 | |
| 470 |
| Thermal Conductivity, W/m-K | 10 | |
| 24 |
| Thermal Expansion, µm/m-K | 14 | |
| 11 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 60 | |
| 9.0 |
| Density, g/cm3 | 8.4 | |
| 7.8 |
| Embodied Carbon, kg CO2/kg material | 10 | |
| 2.9 |
| Embodied Energy, MJ/kg | 140 | |
| 42 |
| Embodied Water, L/kg | 260 | |
| 100 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 200 | |
| 130 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 170 | |
| 830 to 1160 |
| Stiffness to Weight: Axial, points | 13 | |
| 14 |
| Stiffness to Weight: Bending, points | 23 | |
| 25 |
| Strength to Weight: Axial, points | 23 | |
| 28 to 31 |
| Strength to Weight: Bending, points | 21 | |
| 24 to 26 |
| Thermal Diffusivity, mm2/s | 2.7 | |
| 6.5 |
| Thermal Shock Resistance, points | 18 | |
| 27 to 30 |
Alloy Composition
| Carbon (C), % | 0 to 0.050 | |
| 0.17 to 0.24 |
| Chromium (Cr), % | 21 to 23.5 | |
| 11 to 12.5 |
| Cobalt (Co), % | 0 to 2.5 | |
| 0 |
| Copper (Cu), % | 1.5 to 2.5 | |
| 0 |
| Iron (Fe), % | 18 to 21 | |
| 83 to 86.7 |
| Manganese (Mn), % | 1.0 to 2.0 | |
| 0.3 to 0.8 |
| Molybdenum (Mo), % | 5.5 to 7.5 | |
| 0.8 to 1.2 |
| Nickel (Ni), % | 36.1 to 51.1 | |
| 0.3 to 0.8 |
| Niobium (Nb), % | 1.8 to 2.5 | |
| 0 |
| Nitrogen (N), % | 0.15 to 0.25 | |
| 0 |
| Phosphorus (P), % | 0 to 0.040 | |
| 0 to 0.025 |
| Silicon (Si), % | 0 to 1.0 | |
| 0.1 to 0.5 |
| Sulfur (S), % | 0 to 0.030 | |
| 0 to 0.015 |
| Tungsten (W), % | 0 to 1.0 | |
| 0.4 to 0.6 |
| Vanadium (V), % | 0 | |
| 0.2 to 0.35 |