N06058 Nickel vs. AWS ERNiFeCr-2
Both N06058 nickel and AWS ERNiFeCr-2 are nickel alloys. They have 76% of their average alloy composition in common. There are 22 material properties with values for both materials. Properties with values for just one material (8, in this case) are not shown.
For each property being compared, the top bar is N06058 nickel and the bottom bar is AWS ERNiFeCr-2.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 220 | |
| 190 |
| Elongation at Break, % | 45 | |
| 28 |
| Poisson's Ratio | 0.29 | |
| 0.29 |
| Shear Modulus, GPa | 86 | |
| 75 |
| Tensile Strength: Ultimate (UTS), MPa | 860 | |
| 1300 |
Thermal Properties
| Latent Heat of Fusion, J/g | 330 | |
| 310 |
| Melting Completion (Liquidus), °C | 1540 | |
| 1460 |
| Melting Onset (Solidus), °C | 1490 | |
| 1410 |
| Specific Heat Capacity, J/kg-K | 420 | |
| 450 |
| Thermal Conductivity, W/m-K | 9.8 | |
| 12 |
| Thermal Expansion, µm/m-K | 12 | |
| 13 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 70 | |
| 75 |
| Density, g/cm3 | 8.8 | |
| 8.3 |
| Embodied Carbon, kg CO2/kg material | 13 | |
| 13 |
| Embodied Energy, MJ/kg | 170 | |
| 190 |
| Embodied Water, L/kg | 310 | |
| 250 |
Common Calculations
| Stiffness to Weight: Axial, points | 14 | |
| 13 |
| Stiffness to Weight: Bending, points | 23 | |
| 23 |
| Strength to Weight: Axial, points | 27 | |
| 43 |
| Strength to Weight: Bending, points | 23 | |
| 32 |
| Thermal Diffusivity, mm2/s | 2.6 | |
| 3.2 |
| Thermal Shock Resistance, points | 23 | |
| 38 |
Alloy Composition
| Aluminum (Al), % | 0 to 0.4 | |
| 0.2 to 0.8 |
| Boron (B), % | 0 | |
| 0 to 0.0030 |
| Carbon (C), % | 0 to 0.010 | |
| 0 to 0.080 |
| Chromium (Cr), % | 20 to 23 | |
| 17 to 21 |
| Cobalt (Co), % | 0 to 0.3 | |
| 0 |
| Copper (Cu), % | 0 to 0.5 | |
| 0 to 0.3 |
| Iron (Fe), % | 0 to 1.5 | |
| 11.6 to 24.6 |
| Manganese (Mn), % | 0 to 0.5 | |
| 0 to 0.35 |
| Molybdenum (Mo), % | 19 to 21 | |
| 2.8 to 3.3 |
| Nickel (Ni), % | 52.2 to 61 | |
| 50 to 55 |
| Niobium (Nb), % | 0 | |
| 4.8 to 5.5 |
| Nitrogen (N), % | 0.020 to 0.15 | |
| 0 |
| Phosphorus (P), % | 0 to 0.015 | |
| 0 to 0.015 |
| Silicon (Si), % | 0 to 0.1 | |
| 0 to 0.35 |
| Sulfur (S), % | 0 to 0.010 | |
| 0 to 0.015 |
| Titanium (Ti), % | 0 | |
| 0.65 to 1.2 |
| Tungsten (W), % | 0 to 0.3 | |
| 0 |
| Residuals, % | 0 | |
| 0 to 0.5 |