N07041 Nickel vs. Monel 400
Both N07041 nickel and Monel 400 are nickel alloys. There are 19 material properties with values for both materials. Properties with values for just one material (13, in this case) are not shown.
For each property being compared, the top bar is N07041 nickel and the bottom bar is Monel 400.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 220 | |
| 160 |
| Elongation at Break, % | 14 | |
| 20 to 40 |
| Fatigue Strength, MPa | 540 | |
| 230 to 290 |
| Shear Strength, MPa | 850 | |
| 370 to 490 |
| Tensile Strength: Ultimate (UTS), MPa | 1400 | |
| 540 to 780 |
| Tensile Strength: Yield (Proof), MPa | 1050 | |
| 210 to 590 |
Thermal Properties
| Melting Onset (Solidus), °C | 1320 | |
| 1300 |
| Specific Heat Capacity, J/kg-K | 450 | |
| 430 |
| Thermal Conductivity, W/m-K | 11 | |
| 23 |
| Thermal Expansion, µm/m-K | 12 | |
| 14 |
Otherwise Unclassified Properties
| Density, g/cm3 | 8.2 | |
| 8.9 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 180 | |
| 140 to 180 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 2510 | |
| 140 to 1080 |
| Stiffness to Weight: Axial, points | 15 | |
| 10 |
| Stiffness to Weight: Bending, points | 25 | |
| 21 |
| Strength to Weight: Axial, points | 47 | |
| 17 to 25 |
| Strength to Weight: Bending, points | 34 | |
| 17 to 21 |
| Thermal Diffusivity, mm2/s | 3.0 | |
| 6.1 |
| Thermal Shock Resistance, points | 38 | |
| 17 to 25 |