N07041 Nickel vs. S15700 Stainless Steel
N07041 nickel belongs to the nickel alloys classification, while S15700 stainless steel belongs to the iron alloys. There are 19 material properties with values for both materials. Properties with values for just one material (14, in this case) are not shown.
For each property being compared, the top bar is N07041 nickel and the bottom bar is S15700 stainless steel.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 220 | |
| 200 |
| Elongation at Break, % | 14 | |
| 1.1 to 29 |
| Fatigue Strength, MPa | 540 | |
| 370 to 770 |
| Shear Strength, MPa | 850 | |
| 770 to 1070 |
| Tensile Strength: Ultimate (UTS), MPa | 1400 | |
| 1180 to 1890 |
| Tensile Strength: Yield (Proof), MPa | 1050 | |
| 500 to 1770 |
Thermal Properties
| Melting Onset (Solidus), °C | 1320 | |
| 1400 |
| Specific Heat Capacity, J/kg-K | 450 | |
| 480 |
| Thermal Conductivity, W/m-K | 11 | |
| 16 |
| Thermal Expansion, µm/m-K | 12 | |
| 11 |
Otherwise Unclassified Properties
| Density, g/cm3 | 8.2 | |
| 7.8 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 180 | |
| 17 to 270 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 2510 | |
| 640 to 4660 |
| Stiffness to Weight: Axial, points | 15 | |
| 14 |
| Stiffness to Weight: Bending, points | 25 | |
| 25 |
| Strength to Weight: Axial, points | 47 | |
| 42 to 67 |
| Strength to Weight: Bending, points | 34 | |
| 32 to 43 |
| Thermal Diffusivity, mm2/s | 3.0 | |
| 4.2 |
| Thermal Shock Resistance, points | 38 | |
| 39 to 63 |