N08332 Stainless Steel vs. EN 1.5537 Steel

Both N08332 stainless steel and EN 1.5537 steel are iron alloys. They have 45% of their average alloy composition in common. There are 25 material properties with values for both materials. Properties with values for just one material (10, in this case) are not shown.

For each property being compared, the top bar is N08332 stainless steel and the bottom bar is EN 1.5537 steel.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 170
160 to 180
Elastic (Young's, Tensile) Modulus, GPa 200
190
Poisson's Ratio 0.28
0.29
Shear Modulus, GPa 76
73
Tensile Strength: Ultimate (UTS), MPa 520
520 to 1760

Thermal Properties

Latent Heat of Fusion, J/g 310
250
Maximum Temperature: Mechanical, °C 1050
400
Melting Completion (Liquidus), °C 1390
1460
Melting Onset (Solidus), °C 1340
1420
Specific Heat Capacity, J/kg-K 480
470
Thermal Conductivity, W/m-K 12
48
Thermal Expansion, µm/m-K 16
13

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 1.7
7.2
Electrical Conductivity: Equal Weight (Specific), % IACS 1.9
8.2

Otherwise Unclassified Properties

Base Metal Price, % relative 32
1.9
Density, g/cm3 8.0
7.8
Embodied Carbon, kg CO2/kg material 5.4
1.4
Embodied Energy, MJ/kg 77
19
Embodied Water, L/kg 190
47

Common Calculations

Stiffness to Weight: Axial, points 14
13
Stiffness to Weight: Bending, points 24
24
Strength to Weight: Axial, points 18
18 to 63
Strength to Weight: Bending, points 18
18 to 41
Thermal Diffusivity, mm2/s 3.1
13
Thermal Shock Resistance, points 12
15 to 52

Alloy Composition

Boron (B), % 0
0.00080 to 0.0050
Carbon (C), % 0.050 to 0.1
0.33 to 0.38
Chromium (Cr), % 17 to 20
0 to 0.3
Copper (Cu), % 0 to 1.0
0 to 0.25
Iron (Fe), % 38.3 to 48.2
97.6 to 98.9
Lead (Pb), % 0 to 0.0050
0
Manganese (Mn), % 0 to 2.0
0.8 to 1.1
Nickel (Ni), % 34 to 37
0
Phosphorus (P), % 0 to 0.030
0 to 0.025
Silicon (Si), % 0.75 to 1.5
0 to 0.3
Sulfur (S), % 0 to 0.030
0 to 0.025
Tin (Sn), % 0 to 0.025
0