N08332 Stainless Steel vs. EN 1.7379 Steel

Both N08332 stainless steel and EN 1.7379 steel are iron alloys. They have 47% of their average alloy composition in common. There are 31 material properties with values for both materials. Properties with values for just one material (4, in this case) are not shown.

For each property being compared, the top bar is N08332 stainless steel and the bottom bar is EN 1.7379 steel.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 170
200
Elastic (Young's, Tensile) Modulus, GPa 200
190
Elongation at Break, % 34
21
Fatigue Strength, MPa 170
320
Poisson's Ratio 0.28
0.29
Shear Modulus, GPa 76
74
Tensile Strength: Ultimate (UTS), MPa 520
670
Tensile Strength: Yield (Proof), MPa 210
460

Thermal Properties

Latent Heat of Fusion, J/g 310
260
Maximum Temperature: Mechanical, °C 1050
460
Melting Completion (Liquidus), °C 1390
1470
Melting Onset (Solidus), °C 1340
1420
Specific Heat Capacity, J/kg-K 480
470
Thermal Conductivity, W/m-K 12
39
Thermal Expansion, µm/m-K 16
13

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 1.7
7.6
Electrical Conductivity: Equal Weight (Specific), % IACS 1.9
8.8

Otherwise Unclassified Properties

Base Metal Price, % relative 32
3.8
Density, g/cm3 8.0
7.8
Embodied Carbon, kg CO2/kg material 5.4
1.8
Embodied Energy, MJ/kg 77
23
Embodied Water, L/kg 190
59

Common Calculations

PREN (Pitting Resistance) 19
5.7
Resilience: Ultimate (Unit Rupture Work), MJ/m3 140
120
Resilience: Unit (Modulus of Resilience), kJ/m3 110
550
Stiffness to Weight: Axial, points 14
13
Stiffness to Weight: Bending, points 24
24
Strength to Weight: Axial, points 18
24
Strength to Weight: Bending, points 18
22
Thermal Diffusivity, mm2/s 3.1
11
Thermal Shock Resistance, points 12
19

Alloy Composition

Carbon (C), % 0.050 to 0.1
0.13 to 0.2
Chromium (Cr), % 17 to 20
2.0 to 2.5
Copper (Cu), % 0 to 1.0
0
Iron (Fe), % 38.3 to 48.2
94.5 to 96.5
Lead (Pb), % 0 to 0.0050
0
Manganese (Mn), % 0 to 2.0
0.5 to 0.9
Molybdenum (Mo), % 0
0.9 to 1.2
Nickel (Ni), % 34 to 37
0
Phosphorus (P), % 0 to 0.030
0 to 0.025
Silicon (Si), % 0.75 to 1.5
0 to 0.6
Sulfur (S), % 0 to 0.030
0 to 0.030
Tin (Sn), % 0 to 0.025
0